Lanxess Durethan® DP BC 310 EF 600065 Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Extruded , Nylon 6, Unreinforced |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® DP BC 310 EF 600065 Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, injection molding and extrusion grade, non-reinforced, elastomer modified, high impact strength, good flowability (Easy Flow)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.117 g/cc | 0.04035 lb/in³ | ISO 1183 |
| Water Absorption | 7.4 % | 7.4 % | Test Sim. to ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0011 cm/cm | 0.0011 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527-1/-2 |
| Elongation at Yield | 3.8 % | 3.8 % | ISO 527-1/-2 |
| Tensile Modulus | 0.790 GPa | 115 ksi | Conditioned; ISO 527-1/-2 |
| 2.30 GPa | 334 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 19.5 J/cm² @Temperature 23.0 °C |
92.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Conditioned; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 140 µm/m-°C | 77.8 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C | 316 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | ISO 75-1/-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Pellets | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Plaskolite Duraplex® 30% I Impact Modified Acrylic Sheet
- Michelman® Michem® Emulsion 13025 Slip and anti-block additive
- Spartech Polycast UF4 Cell Cast Acrylic
- Constellium PLAN 6061 Aluminum Rolled Plate
- Colorite Polymers CS6023GP Wire and Cable Insulation Vinyl Compound
- Chem Polymer Chemlon 223 Nylon 6, Nucleated
- ATI Allegheny Ludlum Altemp® 718 Nickel-Base Superalloy, Solution Treated plus Precipitation Heat Treated, UNS N07718
Copyright © lookpolymers.com All Rights Reserved