Lanxess Durethan® BKV 50 H2.0 EF 000000 Nylon 6, 50% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 50 H2.0 EF 000000 Nylon 6, 50% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, injection molding grade, 50% glass fibers, good heat-ageing resistance, low viscosity (easy flow)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0019 cm/cm | 0.0019 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0051 cm/cm | 0.0051 in/in | ISO 294-4, 2577 |
| Melt Flow | 36 g/10 min @Load 5.00 kg, Temperature 270 °C |
36 g/10 min @Load 11.0 lb, Temperature 518 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 210 MPa | 30500 psi | ISO 527-1/-2 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527-1/-2 |
| Tensile Modulus | 16.0 GPa | 2320 ksi | ISO 527-1/-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1/-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Features | Heat stabilized or stable to heat | |
| Form | Pellets | |
| ISO Shortname | ISO1874-PA6, MHR, 10-160, GF50 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3865A TPE, PP Overmold or Standalone use
- ND Industries 301 Surface Insensitive Instant Superglue
- Nitriflex NP-1021 Powdered Nitrile
- Petroquimica Triunfo Trithene® JX 7065 LDPE - Injection Molding and Master Batch
- Huntsman Araldite GT 6450 Bisphenol A Epoxy Solid Resin
- ExxonMobil Mobilith AW Series 0
- CP-Polymer-Technik Wellamid® 6600 MZ 315 CP Combination Nylon 66, Conditioned
- Clariant PA213N40 Nylon 6, Mineral/Glass Reinforced, Heat Stabilized, Lubricated
- E-Polymers SEPAZ® LA60 PA66 LFT Resin
Copyright © lookpolymers.com All Rights Reserved