LNP Thermocomp® LF-1006 MG Polyetheretherketone, Glass milled Glass Fiber  (discontinued **)

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Thermocomp® LF-1006 MG Polyetheretherketone, Glass milled Glass Fiber  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Low WarpageForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.53 g/cc
1.53 g/cc
Method A; ASTM D792
Mechanical Properties Metric English Comments
Tensile Strength at Break 139 MPa
20200 psi
ASTM D638
Elongation at Break 2.2 %
2.2 %
ASTM D638
Tensile Modulus 9.72 GPa
1410 ksi
ASTM D638
Flexural Strength 207 MPa
30000 psi
ASTM D790
Flexural Modulus 9.38 GPa
1360 ksi
ASTM D790
Izod Impact, Notched 0.267 J/cm

@Thickness 3.18 mm
0.500 ft-lb/in

@Thickness 0.125 in
ASTM D256
Processing Properties Metric English Comments
Melt Temperature 379 - 388 °C
714 - 730 °F
Mold Temperature 135 - 163 °C
275 - 325 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Moisture Content 0.10 %
0.10 %
Suggested
Back Pressure 0.345 - 0.689 MPa
50.0 - 99.9 psi