- LNP Thermocomp® JF-1006 E LE BK8-055 Polyethersulfone, Glass Fiber Reinforcement (discontinued **)
LNP Thermocomp® JF-1006 E LE BK8-055 Polyethersulfone, Glass Fiber Reinforcement (discontinued **)
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LNP Thermocomp® JF-1006 E LE BK8-055 Polyethersulfone, Glass Fiber Reinforcement
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: High Viscosity, Low ExtractablesForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.61 g/cc | 1.61 g/cc | Method A; ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | at 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 113 MPa | 16400 psi | ASTM D638 |
| Tensile Strength, Yield | 113 MPa | 16400 psi | ASTM D638 |
| Elongation at Break | 1.8 % | 1.8 % | ASTM D638 |
| Elongation at Yield | 1.8 % | 1.8 % | ASTM D638 |
| Tensile Modulus | 9.79 GPa | 1420 ksi | ASTM D638 |
| Flexural Strength | 172 MPa | 24900 psi | ASTM D790 |
| Flexural Modulus | 9.24 GPa | 1340 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm @Thickness 3.18 mm |
1.10 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 4.32 J/cm @Thickness 3.18 mm |
8.09 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Notched (ISO) | 6.80 kJ/m² | 3.24 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | 29.9 kJ/m² | 14.2 ft-lb/in² | ISO 180 |
| Falling Dart Impact | 12.8 J | 9.44 ft-lb | ASTM D3763 |
| Impact Test | 2.70 J | 1.99 ft-lb | Multi-Axial Instrumented Impact Energy; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 29.0 µm/m-°C @Temperature 20.0 °C |
16.1 µin/in-°F @Temperature 68.0 °F |
TMA; ASTM E831 |
| CTE, linear, Transverse to Flow | 36.0 µm/m-°C @Temperature 20.0 °C |
20.0 µin/in-°F @Temperature 68.0 °F |
TMA; ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C | 414 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 354 - 371 °C | 669 - 700 °F | |
| Mold Temperature | 135 - 149 °C | 275 - 300 °F | |
| Drying Temperature | 121 - 149 °C | 250 - 300 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.050 % | 0.050 % | Suggested |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 99.9 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA - 51 LL General Purpose Acrylic Resin
- Overview of materials for Styrenic TPE (Unverified Data**)
- IRPC Polimaxx Porene KU200 Acrylonitrile Butadiene Styrene
- LyondellBasell Petrothene® NA940094 Low Density Polyethylene (Film Grade)
- Solvay TECHNYL® C 246 V 30 PA6, 30% glass fiber, DRY
- Tra-Con Tra-Bond 2143G Medium Viscosity Polyamide Epoxy Adhesive
- American Elements Silicon Oxide Nanopowder
- Anderman Ceramics EA995 Sintered Alumina, 99.5%
- PolyOne Synprene® RT-3840MS Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved