LNP Lubricomp® QFL-4536 Polyamide 6/10 Copolymer, Glass Fiber Reinforced, PTFE + Silicone Lubricant  (disconti

Category Polymer , Thermoplastic , Nylon , Nylon 610
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Lubricomp® QFL-4536 Polyamide 6/10 Copolymer, Glass Fiber Reinforced, PTFE + Silicone Lubricant  (disconti.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.44 g/cc
1.44 g/cc
Method A; ASTM D792
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 137 MPa
19900 psi
ASTM D638
Elongation at Break 2.8 %
2.8 %
ASTM D638
Flexural Strength 207 MPa
30000 psi
ASTM D790
Flexural Modulus 8.62 GPa
1250 ksi
ASTM D790
Izod Impact, Notched 0.907 J/cm

@Thickness 3.18 mm
1.70 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 9.07 J/cm

@Thickness 3.18 mm
17.0 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 202 °C
396 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 268 - 274 °C
514 - 525 °F
Mold Temperature 82.2 - 93.3 °C
180 - 200 °F
Drying Temperature 82.2 °C
180 °F
Dry Time 4 hour
4 hour
Moisture Content 0.20 %
0.20 %
Suggested
Back Pressure 0.172 - 0.345 MPa
24.9 - 50.0 psi