Kraton® D1164 P (SIS) Linear Triblock Copolymer

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer Kraton
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kraton® D1164 P (SIS) Linear Triblock Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Kraton D1164 P is a clear, linear triblock copolymer based on styrene and isoprene with a polystyrene content of 29%. It is supplied from North America in the physical form identified: Kraton D1164 PT - supplied as a dusted dense pelletRegion: Asia Pacific, Europe, Japan, North America, and South AmericaUses: Kraton D1164 P is used in compound formulations and as a modifier of thermoplastics. It may also find use in formulating adhesives, sealants, coatings and modified bitumens.Applications: Adhesives, Sealant and Coatings; Compounding and Personal Hygiene; Impact Modification; Footwear; and Bitumen ModificationNote 1) Primary antioxidant is a non-staining, phenolic antioxidant. The antioxidant package also contains a non-TNPP secondary antioxidant at a target level of 0.2%Information provided by Kraton®
Physical Properties Metric English Comments
Volatiles <= 0.50 %
<= 0.50 %
KM 04
Viscosity 200 - 400 cP
200 - 400 cP
25% Toluene Solution at 25°C; BAM 922
Melt Flow 8.0 - 15 g/10 min

@Load 5.00 kg,
Temperature 200 °C
8.0 - 15 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ASTM D1238
Ash 0.15 - 0.40 %
0.15 - 0.40 %
Talc; BAM 908
Mechanical Properties Metric English Comments
Hardness, Shore A 53

@Time 10.0 sec
53

@Time 0.00278 hour
ASTM D2240
Tensile Strength 27.58 MPa
4000 psi
BAM 1245
Elongation at Break 1000 %
1000 %
BAM 1245
300% Modulus 0.00307 GPa
0.445 ksi
BAM 1245
Descriptive Properties Value Comments
Content Antioxidant
0.08-0.3%, See note 1), KM 08
Polystyrene
27.5-30.5%, KM 03
Total Extractables
<1.0%, KM 05
Styrene/Rubber Ratio 29/71