Kolon SPESIN® KP513UG PBT Alloy Resin
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Extrusion Grade |
| Manufacturer | Kolon |
| Trade Name | SPESIN® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon SPESIN® KP513UG PBT Alloy Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Extrudable, delusteringApplications: Mono filamentInformation provided by API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.080 % | 0.080 % | 60% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.015 - 0.019 cm/cm | 0.015 - 0.019 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 114 | 114 | ASTM D785 |
| Tensile Strength | 68.0 MPa | 9860 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Flexural Strength | 79.0 MPa | 11500 psi | ASTM D790 |
| Flexural Modulus | 0.196 GPa | 28.4 ksi | ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm | 0.918 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 40.0 µm/m-°C | 22.2 µin/in-°F | ASTM D696 |
| Melting Point | 224 °C | 435 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.7 | 3.7 | ASTM D150 |
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | ASTM D149 |
| Arc Resistance | 110 sec | 110 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Abatron 82098 A/B Filled Potting Compound (discontinued **)
- Nitriflex N-615B NBR - Nitrile Rubber
- Total Evatane® 28 - 05 HDPE vinyl acetate copolymer, blown film, injection molding (discontinued **)
- Kolon ELLAS K-590A Caprolactone Based Thermoplastic Polyurethane
- Karina 42/155-RG-GE (CS) Red Color Concentrate for PVC
- Shandong Rike Chemical HELIâ„¢ HPA-220-2 PVC Processing Aid Series (PA)
- Saint-Gobain CHR® M69 Polyester Film Backing Acrylic Adhesive Pressure Sensitive Tape
- A. Schulman POLYBATCH™ Green 3373 Concentrate Based In Polyethylene
- A. Schulman POLYBATCH™ Dark Grey 80431U Concentrate Based In LLDPE
- Chesterton 278 Super Solv
Copyright © lookpolymers.com All Rights Reserved