Isoflon PC Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Extruded |
| Manufacturer | Isoflon |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Isoflon PC Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Good impact resistance among transparent materialsInformation provided by Isoflon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | DIN 53479 |
| Water Absorption | 0.15 % | 0.15 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 75 | 75 | ASTM D785 |
| Tensile Strength | 70.0 MPa | 10200 psi | DIN 53455 |
| Elongation at Break | 50 % | 50 % | DIN 53455 |
| Tensile Modulus | 2.30 GPa | 334 ksi | DIN 53457 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 65.0 µm/m-°C | 36.1 µin/in-°F | DIN 52328 |
| Thermal Conductivity | 0.210 W/m-K | 1.46 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 220 °C | 428 °F | DIN 53736 |
| Maximum Service Temperature, Air | 115 °C | 239 °F | Continuous; DIN 52612 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | |
| Minimum Service Temperature, Air | -60.0 °C | -76.0 °F | Continuous; DIN 52612 |
| Flammability, UL94 | V-0 @Thickness 6.00 mm |
V-0 @Thickness 0.236 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | DIN 53482 |
| Dielectric Constant | 3.0 @Frequency 1000 Hz |
3.0 @Frequency 1000 Hz |
DIN 53483 |
| Dielectric Strength | 28.0 - 30.0 kV/mm | 711 - 762 kV/in | DIN 53481 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Transparent |
Users viewing this material also viewed the following:
- Palm Labs Adhesives Turbo Fuse Series 115SI Surface Insensitive (20 Viscosity) Rapid Bonding Adhesive
- Lucite International Diakon® CLH952L Acrylic Polymer
- Haynes Hastelloy® C-22® alloy, 10% cold worked sheet
- SABIC Innovative Plastics LNP THERMOCOMP WH0200B PBT
- A. Schulman CP842-01 Hexene Copolymer LLDPE Resin
- ExxonMobil Oppalyte™ 40MW648 OPP Film
- Aclo Accutech Polypropylene Homopolymer HP0334M20L Mica Reinforced
- 3M Scotch® 880MSR Filament Tape
- A. Schulman POLYTROPE™ TPP 1024E-01 Olefinic Elastomer For Sheet Extrusion
- PolyOne Synprene® IT 37-031 Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved