Inno-Comp INNOPOL® CS 2-8000 Polypropylene Block-Copolymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer
Manufacturer Inno-Comp Ltd
Trade Name INNOPOL® CS
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Inno-Comp INNOPOL® CS 2-8000 Polypropylene Block-Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
INNOPOL® CS 2-8000 is a polypropylene block-copolymer. This grade is available in nature and custom colored form.INNOPOL® CS 2-8000 is highly suitable for pipe manufacturing where the required property is high impact resistance besides good stiffness.All information provided by INNO-COMP.
Physical Properties Metric English Comments
Density 0.900 g/cc

@Temperature 23.0 °C
0.0325 lb/in³

@Temperature 73.4 °F
ISO 1183
Melt Flow 0.40 g/10 min

@Load 2.16 kg,
Temperature 230 °C
0.40 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 28.0 MPa
4060 psi
50 mm/min; ISO 527-1,-2
Elongation at Yield 10 %
10 %
50 mm/min; ISO 527-1,-2
Tensile Modulus 1.30 GPa
189 ksi
1 mm/min; ISO 527-1,-2
Flexural Modulus 1.40 GPa
203 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 6.20 kJ/m²

@Temperature -20.0 °C
2.95 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
59.0 kJ/m²

@Temperature 23.0 °C
28.1 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Charpy Impact, Notched 0.520 J/cm²

@Temperature -20.0 °C
2.47 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
6.50 J/cm²

@Temperature 23.0 °C
30.9 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 87.0 °C
189 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 48.0 °C
118 °F
ISO 75-1,-2
Vicat Softening Point 79.0 °C
174 °F
B120; ISO 306
150 °C
302 °F
A120; ISO 306
Descriptive Properties Value Comments
Color Natural