- Inno-Comp INNOPOL® CS 2-3120 BPLU 9H0017 20% Talc-Filled, UV Stabilized Polypropylene Block-Copolymer
Inno-Comp INNOPOL® CS 2-3120 BPLU 9H0017 20% Talc-Filled, UV Stabilized Polypropylene Block-Copolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® CS |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Inno-Comp INNOPOL® CS 2-3120 BPLU 9H0017 20% Talc-Filled, UV Stabilized Polypropylene Block-Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
INNOPOL® CS 2-3120 BPLU 9H0017 is a 20% talc filled, UV stabilized compound based on polypropylene block-copolymer.INNOPOL® CS 2-3120 BPLU 9H0017 is developed for producing injection molded automotive components.All information provided by INNO-COMP.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc @Temperature 23.0 °C |
0.0379 lb/in³ @Temperature 73.4 °F |
ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm | 0.010 in/in | ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294 |
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 230 °C |
13 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Ash | 20 % @Temperature 600 °C |
20 % @Temperature 1110 °F |
ISO 3451-1/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 15 % | 15 % | ISO 527-1,-2 |
| Elongation at Yield | 3.5 % | 3.5 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 2.53 GPa | 367 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 2.74 GPa | 397 ksi | 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | 2.50 J/cm² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.150 J/cm² @Temperature -30.0 °C |
0.714 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.400 J/cm² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | DSC; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
FMVSS 302 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Automotive Materials | Pass | FMVSS 302 |
| Color | Black 9H0017 |
Users viewing this material also viewed the following:
- PolyOne OnForce™ LFT PP-50LGF/001 Natural Polypropylene Homopolymer (PP Homopolymer)
- Polimersan Plastics POLIPOLEN® (Polyethylene) HD-PE 500
- Kingfa FW-620 Flame Retardant ABS
- Kolon KOPET® KP133G30 FR-PET Resin
- LTL Color Compounds ColorFast® FRPBT150 PBT, 13% Glass-Filled, Flame Retarded
- Lubrizol Advanced Materials Pearlstick® 46-10/01 Linear Thermoplastic Polyurethane Elastomer
- ExxonMobil Label-Lyte™ 38LW280 OPP Film
- DuPont Teijin Films Mylar® LBTW Polyester Film, 75 Gauge
- ATI Allegheny Ludlum Stainless Steel Chromium-Nickel Type 302, 30% Cold Rolled (UNS S30200)
Copyright © lookpolymers.com All Rights Reserved