- Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
- Ineos ABS Lustran® H801
Ineos ABS Lustran® H801
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® H801.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High heat resistance, PC modified, low emission, increased flow.,Property data per ISO test methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | |
| Melt Flow | 10 g/10 min @Load 10.0 kg, Temperature 220 °C |
10 g/10 min @Load 22.0 lb, Temperature 428 °F |
Estimated using room temperature density |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | |
| Elongation at Yield | 3.0 % | 3.0 % | |
| Tensile Modulus | 2.40 GPa | 348 ksi | |
| Charpy Impact Unnotched | 22.0 J/cm² | 105 ft-lb/in² | |
| 16.0 J/cm² @Temperature -30.0 °C |
76.1 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 3.00 J/cm² | 14.3 ft-lb/in² | |
| 1.20 J/cm² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 0.800 µm/m-°C @Temperature 20.0 °C |
0.444 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | |
| Vicat Softening Point | 105 °C | 221 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 3.0 @Frequency 1e+6 Hz |
3.0 @Frequency 1e+6 Hz |
|
| 3.1 @Frequency 100 Hz |
3.1 @Frequency 100 Hz |
||
| Dielectric Strength | 38.0 kV/mm | 965 kV/in | |
| Dissipation Factor | 0.0050 @Frequency 100 Hz |
0.0050 @Frequency 100 Hz |
|
| 0.0090 @Frequency 1e+6 Hz |
0.0090 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- Nyco NYAD® 5000 Wollastonite
- Rotuba 860S Ethyl Cellulose
- MetalTek MTEK SD100 Cast UNS J93380 Duplex Stainless Steel
- Heatbath/Park Pack Carburizer BF#21
- LyondellBasell Lupolen® 1810 E LDPE
- A. Schulman PP 1407L-01 Polypropylene High-Impact Copolymer Polypropylene
- A. Schulman POLYFLAM™ RCP 505C Flame Retardant Concentrate Based In Low-Density Polyethylene
- Fainplast Compounds HL 84 Flexible PVC, Insulation for High Temperatures
Copyright © lookpolymers.com All Rights Reserved