Ineos ABS Lustran® Guardian™ 732 ABS, Extrusion Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® Guardian™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® Guardian™ 732 ABS, Extrusion Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lustran® Guardian™ ABS 732 is an extrusion grade resin designed for use in thermoformed refrigerator and freezer liner applications. It is suitable for use with 245fa PU foams.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | white; ASTM-D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 82 | 82 | ASTM-D785 |
| Tensile Strength at Break | 28.3 MPa | 4100 psi | ASTM-D638 |
| Tensile Strength, Yield | 22.8 MPa | 3300 psi | ASTM-D638 |
| Elongation at Break | 100 % | 100 % | ASTM-D638 |
| Elongation at Yield | >= 1.0 % | >= 1.0 % | 50:50 CO/OA, Critical; Stolki Method |
| Tensile Modulus | 2.30 GPa | 333 ksi | ASTM-D638 |
| Izod Impact, Notched | 0.747 J/cm @Temperature -17.8 °C |
1.40 ft-lb/in @Temperature 0.000 °F |
1/2" x 1/8"; ASTM-D256 |
| 1.98 J/cm @Temperature 22.8 °C |
3.70 ft-lb/in @Temperature 73.0 °F |
1/2" x 1/8"; ASTM-D256 | |
| Impact Test | 16.3 J @Temperature -17.8 °C |
12.0 ft-lb @Temperature 0.000 °F |
Multiaxial Impact, Total Energy; CEAST |
| 33.9 J @Temperature 22.8 °C |
25.0 ft-lb @Temperature 73.0 °F |
Multiaxial Impact, Total Energy; CEAST |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 72.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
40.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM-D696 |
| Maximum Service Temperature, Air | 60.0 °C @Thickness 1.52 mm |
140 °F @Thickness 0.0600 in |
UL94 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.8 °C | 190 °F | Annealed (2 hours @ 176°F); ASTM-D648 |
| Flammability, UL94 | HB @Thickness 1.016 mm |
HB @Thickness 0.04000 in |
Users viewing this material also viewed the following:
- Global GAB-130 30% Glass Reinforced, General Purpose ABS
- Industrial Laminates/Norplex NP193M Synthetic Fabric Base Grade
- SABIC Innovative Plastics LNP LUBRICOMP UX95672 PPA
- Spartech Royalite R86 PVC Acrylic Weather Resistant Sheet
- EMS-Grivory Grivory® XE 4106 black 9992 PA612-GF30
- Arlon 51580R015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Overview of materials for Polyethersulfone, Carbon Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved