Ineos ABS Lustran® ABS 680 LNS503 High Performance Injection Molding Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® ABS 680 LNS503 High Performance Injection Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lustran® ABS 680 LNS503 is an easy flow version. It is a high performance injection molding grade used for refrigerator and freezer door end caps.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ISO 294-4 |
| Melt Flow | 10 g/10 min @Load 10.0 kg, Temperature 220 °C |
10 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 114 | 114 | ISO 2039-2 |
| Tensile Strength at Break | 37.0 MPa | 5370 psi | 50 mm/min; ISO 527-1,-2 |
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 25 % | 25 % | 50 mm/min; acc. ISO 527-1,-2 |
| Tensile Modulus | 2.60 GPa | 377 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 72.0 MPa | 10400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.50 GPa | 363 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A |
| 16.0 kJ/m² @Temperature -20.0 °C |
7.61 ft-lb/in² @Temperature -4.00 °F |
ISO 180-1A | |
| 23.0 kJ/m² @Temperature 23.0 °C |
10.9 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 96.0 °C | 205 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ISO 75-1,-2 |
| Vicat Softening Point | 102 °C @Load 5.10 kg |
216 °F @Load 11.2 lb |
120°C/hour; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 85 % | 85 % | Angle 60°; ISO 2813 |
Users viewing this material also viewed the following:
- MV Labs AU160 AuCN Gold(I) cyanide
- PolyOne OnFlex™ U 5380A-S0013 Thermoplastic Elastomer (TPE)
- Overview of materials for Nylon 12, PTFE Filled
- Johnson Matthey Matti-sil 453 Cadmium Free Brazing Alloy
- LG Chemical Lupox® GP2156FT PBT+GF15%
- Styron Magnumâ„¢ 3416 SC Natural Plus ABS Resin
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR N650 Filler
- Daelim H&L Plavis-MS CM MoS2 Filled Aromatic Polyimide Bearing
- Polikim KESTAMID® HS Polyamide 6, Heat Resistant
Copyright © lookpolymers.com All Rights Reserved