Industrial Laminates/Norplex SP525M (WaveMax 5000) Glass Fabric

Category Polymer , Thermoset
Manufacturer Industrial Laminates/Norplex
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex SP525M (WaveMax 5000) Glass Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Non-woven substrate combined with high temperature, static dissipative epoxy resin. Superior machining properties. Capable of producing thin walls with high strength for finely machined parts. Excellent mechanical strength at elevated temperatures. The continuous operating temperature is 190°C.Short excursions to temperatures approaching 360°C, such as in wave soldering or IR re-flow, will not adversely affect the life of this material.Thickness Tested: 0.062" & 0.315"
Physical Properties Metric English Comments
Specific Gravity 1.75 - 1.85 g/cc
1.75 - 1.85 g/cc
Moisture Absorption at Equilibrium 0.070 %

@Thickness 8.00 mm
 0.070 %

@Thickness 0.315 in
Mechanical Properties Metric English Comments
Hardness, Rockwell M 100 - 120
100 - 120
Tensile Strength, Yield 117 MPa

@Thickness 8.00 mm
 17000 psi

@Thickness 0.315 in
 CW
159 MPa

@Thickness 8.00 mm
 23000 psi

@Thickness 0.315 in
 LW
Flexural Strength 79.3 MPa

@Thickness 8.00 mm
 11500 psi

@Thickness 0.315 in
 at Elevated Temperature (CW E-1/150, T-150)
93.8 MPa

@Thickness 8.00 mm
 13600 psi

@Thickness 0.315 in
 at Elevated Temperature (CW E-1/150, T-150)
179 MPa

@Thickness 8.00 mm
 26000 psi

@Thickness 0.315 in
 CW
207 MPa

@Thickness 8.00 mm
 30000 psi

@Thickness 0.315 in
 LW
Flexural Modulus 14.5 GPa

@Thickness 8.00 mm
 2100 ksi

@Thickness 0.315 in
 CW
15.2 GPa

@Thickness 8.00 mm
 2200 ksi

@Thickness 0.315 in
 LW
Compressive Strength 345 MPa

@Thickness 8.00 mm
 50000 psi

@Thickness 0.315 in
 Flatwise
Izod Impact, Unnotched 2.40 J/cm

@Thickness 8.00 mm
 4.50 ft-lb/in

@Thickness 0.315 in
 CW, E-48/50
2.67 J/cm

@Thickness 8.00 mm
 5.00 ft-lb/in

@Thickness 0.315 in
 LW, E-48/50
Thermal Properties Metric English Comments
CTE, linear 22.1 µm/m-°C

@Temperature 20.0 °C
 12.3 µin/in-°F

@Temperature 68.0 °F
 x-axis
CTE, linear, Transverse to Flow 22.5 µm/m-°C

@Temperature 20.0 °C
 12.5 µin/in-°F

@Temperature 68.0 °F
 y-axis
24.7 µm/m-°C

@Temperature 20.0 °C
 13.7 µin/in-°F

@Temperature 68.0 °F
 z-axis
Maximum Service Temperature, Air 275 °C
527 °F
Continuous Operating Temperature
Electrical Properties Metric English Comments
Volume Resistivity 10000 - 1.00e+11 ohm-cm
10000 - 1.00e+11 ohm-cm
Surface Resistivity per Square 1e+05 - 1.00e+9 ohm
1e+05 - 1.00e+9 ohm
Descriptive Properties Value Comments
Resin Degradation Temperature 360°C