Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Industrial Laminates/Norplex P95 Glass Fabric

Category Polymer , Thermoset
Manufacturer Industrial Laminates/Norplex
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex P95 Glass Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Woven glass fabric with polyimide resin engineered to maintain excellent physical properties at 240°C. Low coefficient of thermal expansion, high mechanical strength.Thickness Tested: 0.062" , 0.125", & 0.500"
Physical Properties Metric English Comments
Specific Gravity 1.84 g/cc
1.84 g/cc
Moisture Absorption at Equilibrium 0.35 %

@Thickness 1.57 mm
 0.35 %

@Thickness 0.0620 in
Mechanical Properties Metric English Comments
Hardness, Rockwell M 110 - 130

@Thickness 1.57 mm
 110 - 130

@Thickness 0.0620 in
Tensile Strength, Yield 276 MPa

@Thickness 3.17 mm
 40000 psi

@Thickness 0.125 in
 CW
331 MPa

@Thickness 3.17 mm
 48000 psi

@Thickness 0.125 in
 LW
Flexural Strength 455 MPa

@Thickness 1.57 mm
 66000 psi

@Thickness 0.0620 in
 CW
538 MPa

@Thickness 1.57 mm
 78000 psi

@Thickness 0.0620 in
 LW
Flexural Modulus 19.3 GPa

@Thickness 1.57 mm
 2800 ksi

@Thickness 0.0620 in
 CW
22.1 GPa

@Thickness 1.57 mm
 3200 ksi

@Thickness 0.0620 in
 LW
Compressive Strength 483 MPa

@Thickness 12.7 mm
 70000 psi

@Thickness 0.500 in
 Flatwise
Shear Strength 186 MPa

@Thickness 1.57 mm
 27000 psi

@Thickness 0.0620 in
 Perpendicular
Izod Impact, Unnotched 4.00 J/cm

@Thickness 12.7 mm
 7.50 ft-lb/in

@Thickness 0.500 in
 CW, E-48/50
6.14 J/cm

@Thickness 12.7 mm
 11.5 ft-lb/in

@Thickness 0.500 in
 LW, E-48/50
Thermal Properties Metric English Comments
CTE, linear 10.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 5.56 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis
CTE, linear, Transverse to Flow 13.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 7.22 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis
Maximum Service Temperature, Air 240 °C
464 °F
Maximum Operating Temperature
Glass Transition Temp, Tg 200 °C
392 °F
Tg
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Dielectric Constant 4.8

@Thickness 1.57 mm
 4.8

@Thickness 0.0620 in
 Permittivity, Cond D-24/23
Dielectric Strength 29.5 kV/mm

@Thickness 1.57 mm
 750 kV/in

@Thickness 0.0620 in
 D-48/50
33.5 kV/mm

@Thickness 1.57 mm
 850 kV/in

@Thickness 0.0620 in
 Condition - A
Dielectric Breakdown 55000 V

@Thickness 1.57 mm
 55000 V

@Thickness 0.0620 in
 D-48/50
65000 V

@Thickness 1.57 mm
 65000 V

@Thickness 0.0620 in
 Condition A
Dissipation Factor 0.010

@Thickness 1.57 mm
 0.010

@Thickness 0.0620 in
 Cond D-24/23
Arc Resistance 130 sec

@Thickness 3.17 mm
 130 sec

@Thickness 0.125 in
 ASTM D495
Comparative Tracking Index 240 V

@Thickness 3.17 mm
 240 V

@Thickness 0.125 in
 ASTM D3638
Descriptive Properties Value Comments
Bond Strength 1,500 lb
0.5"
Users viewing this material also viewed the following: