Industrial Laminates/Norplex NP319 Cotton Fabric Base Laminate

Category Polymer , Thermoset , Phenolic
Manufacturer Industrial Laminates/Norplex
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex NP319 Cotton Fabric Base Laminate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Bleached canvas combined with phenolic resin and graphite lubricant. Better moisture resistance and machining characteristics than NP315.
Physical Properties Metric English Comments
Specific Gravity 1.35 - 1.45 g/cc

@Thickness 1.57 mm
 1.35 - 1.45 g/cc

@Thickness 0.0620 in
 ASTM D792
Moisture Absorption at Equilibrium 2.5 %

@Thickness 1.57 mm
 2.5 %

@Thickness 0.0620 in
 ASTM D229
Mechanical Properties Metric English Comments
Hardness, Rockwell M 90 - 110

@Thickness 1.57 mm
 90 - 110

@Thickness 0.0620 in
 ASTM D785
Tensile Strength, Yield 62.1 MPa

@Thickness 1.57 mm
 9000 psi

@Thickness 0.0620 in
 CW; ASTM D638
75.8 MPa

@Thickness 1.57 mm
 11000 psi

@Thickness 0.0620 in
 LW; ASTM D638
Modulus of Elasticity 6.89 GPa

@Thickness 1.57 mm
 1000 ksi

@Thickness 0.0620 in
 CW; ASTM D229
8.96 GPa

@Thickness 1.57 mm
 1300 ksi

@Thickness 0.0620 in
 LW; ASTM D229
Flexural Strength 124 MPa

@Thickness 1.57 mm
 18000 psi

@Thickness 0.0620 in
 CW; ASTM D790
138 MPa

@Thickness 1.57 mm
 20000 psi

@Thickness 0.0620 in
 LW; ASTM D790
Compressive Strength 248 MPa

@Thickness 12.7 mm
 36000 psi

@Thickness 0.500 in
 ASTM D695
Shear Strength 89.6 MPa

@Thickness 15.7 mm
 13000 psi

@Thickness 0.620 in
 ASTM D732
Izod Impact, Unnotched 0.988 J/cm

@Thickness 12.7 mm
 1.85 ft-lb/in

@Thickness 0.500 in
 CW, Cond E-48/50; ASTM D256
1.07 J/cm

@Thickness 12.7 mm
 2.00 ft-lb/in

@Thickness 0.500 in
 LW, Cond E-48/50; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 18.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 10.0 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
CTE, linear, Transverse to Flow 22.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 12.2 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
Maximum Service Temperature, Air 150 °C
302 °F
Flammability, UL94 HB

@Thickness 1.57 mm
 HB

@Thickness 0.0620 in
Descriptive Properties Value Comments
Bond Strength 1700 lb
0.5", ASTM D229
Color Natural, Black