- Industeel CLC 1.2312 Prehardened Mold Steel (300HB/32HRC) with Improved Machinability
Industeel CLC 1.2312 Prehardened Mold Steel (300HB/32HRC) with Improved Machinability
| Category | Metal , Ferrous Metal , Carbon Steel , High Carbon Steel , Tool Steel , Mold Steel |
| Manufacturer | Groupe Arcelor |
| Trade Name | CLC |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Industeel CLC 1.2312 Prehardened Mold Steel (300HB/32HRC) with Improved Machinability.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: CLC 1.2312 is a chromium-manganese-molybdenum grade designed for plastic mold industry. This grade is normally delivered in a prehardened condition at a hardness level of 300HB/32HRC. The grade has a fully homogeneous martensite-bainite microstructure. CLC 1.2312 grade has specific sulfur addition (0.060% typical) in order to increase strongly it's machinability. Compared to CLC 1.2311 grade 30% increase in milling speed and 300% increase in drilling speed can be expected. At constant cutting speed, tool life is multiplied by a least 5 when replacing CLC 1.2311 by CLC1.2312 grade.Information provided by manufacturer.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 300 | 300 | Typical, in Longitudinal and Transverse Direction |
| Tensile Strength, Ultimate | 990 MPa | 144000 psi | Typical, Transverse Direction |
| 1010 MPa | 146000 psi | Typical, Longitudinal Direction | |
| Tensile Strength, Yield | 820 MPa @Strain 0.200 % |
119000 psi @Strain 0.200 % |
Typical, Transverse Direction |
| 850 MPa @Strain 0.200 % |
123000 psi @Strain 0.200 % |
Typical, Longitudinal Direction | |
| Elongation at Break | 9.0 % | 9.0 % | Typical, Transverse Direction |
| 10 % | 10 % | Typical, Longitudinal Direction | |
| Modulus of Elasticity | 205 GPa | 29700 ksi | Typical, in Longitudinal and Transverse Direction |
| Charpy Impact | 15.0 J | 11.1 ft-lb | Typical (Transverse) |
| 25.0 J | 18.4 ft-lb | Typical (Longitudinal) | |
| 15.0 J @Temperature -20.0 °C |
11.1 ft-lb @Temperature -4.00 °F |
Typical (Longitudinal) | |
| Charpy Impact, Unnotched | 20.0 J @Temperature 20.0 °C |
14.8 ft-lb @Temperature 68.0 °F |
Transverse |
| 25.0 J @Temperature -20.0 °C |
18.4 ft-lb @Temperature -4.00 °F |
Longitudinal | |
| 30.0 J @Temperature 20.0 °C |
22.1 ft-lb @Temperature 68.0 °F |
Longitudinal |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 11.5 µm/m-°C @Temperature 20.0 - 100 °C |
6.39 µin/in-°F @Temperature 68.0 - 212 °F |
|
| 11.57 µm/m-°C @Temperature 20.0 - 200 °C |
6.428 µin/in-°F @Temperature 68.0 - 392 °F |
||
| 12.47 µm/m-°C @Temperature 20.0 - 300 °C |
6.928 µin/in-°F @Temperature 68.0 - 572 °F |
||
| Thermal Conductivity | 34.0 W/m-K @Temperature 20.0 °C |
236 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.40 % | 0.40 % | |
| Chromium, Cr | 1.9 % | 1.9 % | |
| Iron, Fe | 95.628 - 95.64 % | 95.628 - 95.64 % | As remainder |
| Manganese, Mn | 1.5 % | 1.5 % | |
| Molybdenum, Mo | 0.20 % | 0.20 % | |
| Phosphorous, P | <= 0.012 % | <= 0.012 % | |
| Silicon, Si | 0.30 % | 0.30 % | |
| Sulfur, S | 0.060 % | 0.060 % |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible XV 3716 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Nilit FRIANYL A63 H Nylon 6.6 for injection molding
- ICO Polymers ICORENEâ„¢ 110-1327 LMDPE Rotational Molding Resin
- Lubriplate SYN-H1-220 Polyalkylene Glycol-Based Synthetic Food Machinery Grade Fluid
- Samsung Cheil Industries Starex® WR-9700S ASA, Unreinforced
- Shinkong Synthetic Fibers Shinite® PP4220 PP, High Impact, Fire Retardant
- Loctite® Gasket Eliminator® 509 Flange Sealant
Copyright © lookpolymers.com All Rights Reserved