Indium Corp. Indalloy 260 Tin Solder Alloy
| Category | Metal , Nonferrous Metal , Solder/Braze Alloy , Tin Alloy |
| Manufacturer | Indium Corporation of America |
| Trade Name | Indalloy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Indium Corp. Indalloy 260 Tin Solder Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information Provided by Indium Corporation
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.32 g/cc | 0.264 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 38.78 MPa | 5625 psi | |
| Elongation at Break | 15.7 % | 15.7 % | |
| Modulus of Elasticity | 14.5 GPa | 2110 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 217 - 226 °C | 423 - 439 °F | |
| Solidus | 217 °C | 423 °F | |
| Liquidus | 226 °C | 439 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Copper, Cu | 0.50 % | 0.50 % | |
| Manganese, Mn | 0.050 % | 0.050 % | Dopant |
| Silver, Ag | 1.0 % | 1.0 % | |
| Tin, Sn | 98.5 % | 98.5 % |
Users viewing this material also viewed the following:
- Resinlab® EP1112NC Black Electronic Grade Epoxy Encapsulant
- Lehmann & Voss LUVOCOM® 1/CF/30/TF/13/SI/2/BK Polyamide 66, with carbon fiber, PTFE, lubricant modified, heat stabilized
- Solvay Specialty Polymers Aquivion® E87-05S Tetrafluoroethylene + SFVE (TFE+SFVE)
- SSAB Tunnplat Docol® 500YP High-strength Steel
- Formosa Plastics Formolene® 3312E Random Copolymer Polypropylene
- DAK Americas Laser+® HS AD600A PET
- China Tungsten YG13C Cemented Tungsten Carbide for Mining Purposes
- EMS-Grivory Grivory® BM 17 PA*
- Asahi Kasei Thermylene® P6-23FG-2600 23% Glass Fiber Reinforced, Heat Stabilized
- 3M Scotch-Seal™ 1252 Tamper Proof Sealant
Copyright © lookpolymers.com All Rights Reserved