IRPC Polimaxx Polene 1111NX TA8 Polypropylene Compound
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | IRPC Polimaxx |
| Trade Name | Polene |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | IRPC Polimaxx Polene 1111NX TA8 Polypropylene Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
CHARACTERISTICS: POLYPROPYLENE HOMOPOLYMER WITH 40% TALCUM REINFORCED HIGH STIFFNESSAPPLICATIONS: INJECTION MOLDING FOR AUTOPARTS, ELECTRICAL APPLIANCES
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ASTM D792 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 101 | 101 | ASTM D785 |
| Tensile Strength, Yield | 35.8 MPa | 5190 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Yield Strength | 54.9 MPa | 7970 psi | ASTM D790 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | ASTM D790 |
| Izod Impact, Notched | 0.216 J/cm @Temperature 23.0 °C |
0.404 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Lord Adhesives Thermosetâ„¢ MD-110 Conductive Adhesive
- Momentive Performance Materials IS808 One-Component, Paste Consistency Silicone Rubber Adhesive Sealant, Translucent
- SABIC Innovative Plastics LNP LUBRILOY KL201 Acetal (Asia Pacific)
- ExxonMobil LL 1001x76 Blown Film Resin
- BASF Ultraform® W2320 U035 LEV POM
- BASF Ultramid® HMG14 HS BK 102 60% Glass Filled PA66 (Conditioned)
- HP Alloys Nitronic® 60 Austenitic Stainless, Level 2 Cold Worked
Copyright © lookpolymers.com All Rights Reserved