Huntsman PE 1302 EVA Film Extrusion  (discontinued **)

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Huntsman PE 1302 EVA Film Extrusion  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3% Vinyl Acetate EVA copolymer and FDA compliantFeatures: High clarity film with good low temperature toughness and heat seal characteristics.Applications: Film extrusion: food packaging, general purpose packaging requiring good low temperature toughness and flexibility.FDA Notes: Conforms to FDA regulation 21 CFR 177.1350 under condition of use C through G described in Table 2 of 21 CFR 176.170Film properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation
Physical Properties Metric English Comments
Density 0.925 g/cc
0.0334 lb/in³
ASTM D1505
Thickness 25.4 microns
1.00 mil
Melt Flow 2.0 g/10 min
2.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 49
49
ASTM D2240
Tensile Strength, Ultimate 13.1 MPa
1900 psi
ASTM D638
Tensile Strength, Yield 9.00 MPa
1310 psi
ASTM D638
Film Elongation at Break, MD 450 %
450 %
ASTM D882
Film Elongation at Break, TD 700 %
700 %
ASTM D882
Elongation at Break 650 %
650 %
ASTM D638
Modulus of Elasticity 0.262 GPa
38.0 ksi
Secant; ASTM D638
Secant Modulus, MD 0.141 GPa
20.5 ksi
ASTM D882
Secant Modulus, TD 0.173 GPa
25.1 ksi
ASTM D882
Dart Drop 5.91 g/micron
150 g/mil
ASTM D1709
Dart Drop Test 150 g
0.331 lb
ASTM D1709
Film Tensile Strength at Break, MD 23.0 MPa
3340 psi
ASTM D882
Film Tensile Strength at Break, TD 17.0 MPa
2470 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 93.0 °C
199 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 4.5 %
4.5 %
ASTM D1003
Gloss 75 %
75 %
at 45°; ASTM D523
Processing Properties Metric English Comments
Melt Temperature 174 - 185 °C