- Honeywell Oxyshieldâ„¢ BOEB Biaxially Oriented, Co-Extruded Nylon 6/EVOH/Nylon 6 Clear Film
Honeywell Oxyshieldâ„¢ BOEB Biaxially Oriented, Co-Extruded Nylon 6/EVOH/Nylon 6 Clear Film
| Category | Polymer , Film , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Film Grade |
| Manufacturer | Honeywell |
| Trade Name | Oxyshield™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell Oxyshieldâ„¢ BOEB Biaxially Oriented, Co-Extruded Nylon 6/EVOH/Nylon 6 Clear Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Oxyshieldâ„¢ BOEB is a 0.60 mil (15 micron) biaxially oriented, coextruded nylon 6/EVOH/nylon 6 clear film having excellent gas barrier through a broad range of relative humidity. The film provides high strength, good chemical resistance, and excellent flavor and aroma barrier for food packaging. Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 100 g/m²/day | 6.44 g/100 in²/day | 104°F (40°C) / 90%RH; ASTM E96 |
| Oxygen Transmission Rate | 1.50 cc/m²/day | 0.0966 cc/100 in²/day | 68°F (20°C) / 65%RH; ASTM D3985 |
| Thickness | 15.2 microns | 0.600 mil | |
| Surface Tension | 36 - 38 dynes/cm | 36 - 38 dynes/cm | untreated side; ASTM D2578 |
| >= 46 dynes/cm | >= 46 dynes/cm | treated side; ASTM D2578 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 110 % | 110 % | ASTM D882 |
| Film Elongation at Break, TD | 100 % | 100 % | ASTM D882 |
| Secant Modulus, MD | 1.60 GPa | 232 ksi | ASTM D882 |
| Secant Modulus, TD | 1.50 GPa | 218 ksi | ASTM D882 |
| Coefficient of Friction | 0.15 | 0.15 | film to stainless steel; ASTM D1894 |
| 0.50 | 0.50 | film to film; ASTM D1894 | |
| Film Tensile Strength at Break, MD | 190 MPa | 27600 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 200 MPa | 29000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 1.6 % | 1.6 % | hot air, 320°F/160°C - 5 min. |
| 2.8 % | 2.8 % | hot water, 203°F/95°C - 5 min. | |
| Shrinkage, TD | 0.30 % | 0.30 % | hot air, 320°F/160°C - 5 min. |
| 1.4 % | 1.4 % | hot water, 203°F/95°C - 5 min. |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 4.0 % | 4.0 % | ASTM D1003 |
| Gloss | 170 % | 170 % | at 20°; ASTM D523 |
| Transmission, Visible | 88 % | 88 % |
Users viewing this material also viewed the following:
- NanoAmor 95%, OD/ID/L: 10-20/5-10 nm/0.5-2 um Short Multi-Walled Carbon Nanotubes
- Materion Beryllium Copper Alloy M25 Wire; 1/4HT (TH01) Temper; 1.3-12.7 mm Diameter (UNS C17300)
- KKPC KOSYN KSL 352 Styrene-Butadiene Latex
- Lehmann & Voss LUVOCOM® 1/GF/40/TF/13 Polyamide 66, with glass fiber and PTFE
- Indium Corp. Indalloy 94 Lead-Tin-Cadmium Solder Alloy
- Lubrizol Advanced Materials PEARLCOAT® DIPP-119 Thermoplastic Polyurethane Elastomer
- Borealis FG5190 Linear Low Density Polyethylene
- Fainplast Compounds PH 58/AL Flexible PVC, Transparent Extrusion
- Unitika EX-1030 PA6, Conditioned
Copyright © lookpolymers.com All Rights Reserved