DuPont Teijin Films Mylar® LBT Polyester Film, 75 Gauge (19 µm)
| Category | Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film |
| Manufacturer | DuPont Teijin Films (DTF) |
| Trade Name | Mylar® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Teijin Films Mylar® LBT Polyester Film, 75 Gauge (19 µm).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by DuPont Packaging Polymers.An uncoated, transparent polyester film that has been corona-treated to provide superior wetting and adhesion to inks, primers, and adhesives. Standard thicknesses include 48, 75, and 92 gauges. Other gauges may be available on special request. Typically used as the reverse printed outer ply of a lamination with inner plies providing additional oxygen barrier if needed, as well as heat sealability.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | Average value for Mylar® films. |
| Moisture Vapor Transmission | 0.600 cc-mm/m²-24hr-atm | 1.52 cc-mil/100 in²-24hr-atm | ASTM E96 Procedure E |
| Water Vapor Transmission | 30.0 g/m²/day | 1.93 g/100 in²/day | ASTM E96 Procedure E |
| Oxygen Transmission | 2.10 cc-mm/m²-24hr-atm | 5.33 cc-mil/100 in²-24hr-atm | or 110 cc/m²-24hr-atm for the film. ASTM D3985 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 130 % | 130 % | ASTM D882 |
| Film Elongation at Break, TD | 100 % | 100 % | ASTM D882 |
| Modulus of Elasticity | 3.79 GPa | 550 ksi | (stiffness), ASTM D882 |
| Tear Strength Test | 400 | 400 | Graves, g; ASTM D1004 |
| Film Tensile Strength at Break, MD | 200 MPa | 29000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 242 MPa | 35100 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 121 °C | 250 °F | May be used to contain foods during baking above this temperature. |
| Shrinkage | 2.2 % @Temperature 150 °C, Time 1800 sec |
2.2 % @Temperature 302 °F, Time 0.500 hour |
Film shrinkage in oven. |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 6.5 % | 6.5 % | ASTM D1003 |
| Gloss | 180 % | 180 % | 20°; ASTM D2457 |
| Transmission, Visible | 73 % | 73 % | % Clarity; ASTM D1746 |
Users viewing this material also viewed the following:
- Polimeri Europa Riblene® FL 34 Low Density Polyethylene - Blown Film Extrusion
- Park Electrochemical Nelco® N8000Q Cyanate Ester Epoxy Laminate and Prepreg
- JPJ Technologies 1500J HDPE Injection
- Saint-Gobain Chemfab® 3 Basic PTFE-Coated Glass
- Teknor Apex APEX® 94-A0098C-90 Polyvinyl Chloride, Flexible
- Total PPH 9040 Polypropylene, Homopolymer
- EMS-Grivory Grivory® BG-50 HM PA6-GF50
- American Computer Optics 12.1in Tempered LCD Glass
- Ashley Polymers Ashlene® LT940H Nylon 11
- Overview of materials for Cellulose Acetate Butyrate, Molded
Copyright © lookpolymers.com All Rights Reserved