Honeywell CapranÂ® Emblemâ„¢ 1500M M-Coated Bi-Axially Oriented Nylon Film

Category	Polymer , Film , Thermoplastic , Nylon
Manufacturer	Honeywell
Trade Name	Capran® Emblem™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Honeywell CapranÂ® Emblemâ„¢ 1500M M-Coated Bi-Axially Oriented Nylon Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: CapranÂ® Emblemâ„¢ 1500M is a bi-axially oriented nylon film. It is a versatile and robust film that satisfies many packaging needs, and has superior resistance to oils, fats, hydrocarbons, and many solvents. It is also microwavable, making it an excellent choice for lidding stock. CapranÂ® Emblemâ„¢ 1500M has a polymeric coating that enhances adhesion to a variety of printing inks, coatings, and adhesives. Applications: bag-on-box packaging, packaging for processed meats, cheese, meat snacks, coffee bricks, coffee bags, and pet food, agricultural bags, stand-up shampoo pouches, book covers and metallized balloons. CapranÂ® Emblemâ„¢ 1500M is also excellent for metallization processes.Information provided by Honeywell.

Physical Properties	Metric	English	Comments
Density	1.16 g/cc	0.0420 lb/inÂ³	Yield Density
Water Vapor Transmission	310 - 357 g/mÂ²/day	20.0 - 23.0 g/100 inÂ²/day	100Â°F / 100%RH); ASTM F1249
Oxygen Transmission Rate	46.56 - 62.08 cc/mÂ²/day	2.998 - 3.998 cc/100 inÂ²/day	77Â°F / 0% / RH; ASTM D3985
Thickness	15.2 microns	0.600 mil

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	60 - 90 %	60 - 90 %	ASTM D882
Film Elongation at Break, TD	60 - 90 %	60 - 90 %	ASTM D882
Secant Modulus, MD	2.41 - 3.52 GPa	350 - 511 ksi	ASTM D882
Secant Modulus, TD	2.275 - 3.45 GPa	330.0 - 500 ksi	ASTM D882
Coefficient of Friction	0.18 - 0.27	0.18 - 0.27	film to stainless steel; ASTM D1894
	0.59 - 0.60	0.59 - 0.60	film to film; ASTM D1894
Tear Strength Test	1100 - 1500	1100 - 1500	graves tear, grams/mil (initial); ASTM D1004
Elmendorf Tear Strength, MD	0.5248 - 0.787 g/micron	13.33 - 20.0 g/mil
Film Tensile Strength at Break, MD	234 - 303 MPa	34000 - 44000 psi	ASTM D882
Film Tensile Strength at Break, TD	193 - 303 MPa	28000 - 44000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Shrinkage, MD	1.4 - 2.4 %	1.4 - 2.4 %	320Â°F / 160Â°C - 5 minutes; ASTM D1204
Shrinkage, TD	0.20 - 0.70 %	0.20 - 0.70 %	320Â°F / 160Â°C - 5 minutes; ASTM D1204

Optical Properties	Metric	English	Comments
Haze	<= 3.3 %	<= 3.3 %	ASTM D1003
Gloss	160 - 175 %	160 - 175 %	at 20Â°