Honeywell ACLAR® 22A (2.00 mil) Copolymer Film  (discontinued **)

Category Polymer , Film , Thermoplastic , Fluoropolymer
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Honeywell ACLAR® 22A (2.00 mil) Copolymer Film  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: ACLAR® 22A is a copolymer film consisting primarily of chlorotrifluoroethylene (CTFE). It is a flexible transparent film used to package moisture sensitive products.Information provided by Honeywell.
Physical Properties Metric English Comments
Specific Gravity 2.08 g/cc
2.08 g/cc
ASTM D1505
Density 2.08 g/cc
0.0750 lb/in³
Yield Density
Water Vapor Transmission 0.300 g/m²/day
0.0193 g/100 in²/day
100°F (37.8°C) / 100%RH; ASTM F1249
Thickness 50.8 microns
2.00 mil
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 115 - 225 %
115 - 225 %
ASTM D882
Film Elongation at Break, TD 200 - 300 %
200 - 300 %
ASTM D882
Secant Modulus, MD 0.965 - 1.103 GPa
140 - 160.0 ksi
ASTM D882
Secant Modulus, TD 1.034 - 1.103 GPa
150.0 - 160.0 ksi
ASTM D882
Tear Strength Test 250 - 325
250 - 325
graves tear TD, grams/mil; ASTM D1004
325 - 350
325 - 350
graves tear MD, grams/mil; ASTM D1004
Film Tensile Strength at Break, MD 51.7 - 75.8 MPa
7500 - 11000 psi
ASTM D882
Film Tensile Strength at Break, TD 34.5 - 55.2 MPa
5000 - 8000 psi
ASTM D882
Thermal Properties Metric English Comments
Thermal Conductivity 0.222 W/m-K
1.54 BTU-in/hr-ft²-°F
Melting Point 190 °C
374 °F
crystalline melting point; ASTM D4591
Oxygen Index 100 %
100 %
ASTM D2863
Shrinkage, MD 12 - 15 %
12 - 15 %
300°F / 149°C - 10 min.; ASTM D1204
Shrinkage, TD -15.0 - -12.0 %
-15.0 - -12.0 %
300°F / 149°C - 10 min.; ASTM D1204
Optical Properties Metric English Comments
Haze <= 1.0 %
<= 1.0 %
ASTM D1003
Transmission, Visible 90 %
90 %
transparent; thickness not quantified
Descriptive Properties Value Comments
Flammability non flammable