Hippe EP GM 203 Glass Mat Reinforced Epoxy Resin - Sheet
| Category | Polymer , Thermoset , Epoxy , Epoxy, Molded, Glass Fiber Filler |
| Manufacturer | Erhard Hippe KG |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hippe EP GM 203 Glass Mat Reinforced Epoxy Resin - Sheet.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.70 - 1.90 g/cc | 1.70 - 1.90 g/cc | IEC 1212-2 8.1 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | >= 250 MPa | >= 36300 psi | IEC 1212-2 5.7 |
| Flexural Strength | >= 160 MPa @Temperature 150 °C |
>= 23200 psi @Temperature 302 °F |
Perpendicular to laminations; IEC 1212-2 5.1 |
| >= 320 MPa @Temperature 23.0 °C |
>= 46400 psi @Temperature 73.4 °F |
Perpendicular to laminations; IEC 1212-2 5.1 | |
| Flexural Modulus | >= 15.0 GPa | >= 2180 ksi | IEC 1212-2 5.2 |
| Compressive Strength | >= 350 MPa | >= 50800 psi | Perpendicular to laminations; IEC 1212-2 5.3 |
| Shear Strength | >= 20.0 MPa | >= 2900 psi | Parallel to laminations; IEC 1212-2 5.6 |
| Izod Impact, Unnotched (ISO) | >= 54.0 kJ/m² | >= 25.7 ft-lb/in² | Parallel to laminations; IEC 1212-2 5.5.3 |
| Charpy Impact Unnotched | >= 5.00 J/cm² | >= 23.8 ft-lb/in² | Parallel to laminations; IEC 1212-2 5.5.2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 5.00e+9 ohm | >= 5.00e+9 ohm | After immersion in water; IEC 1212-2 6.3 |
| Dielectric Constant | <= 5.5 @Frequency 48.0 - 62.0 Hz |
<= 5.5 @Frequency 48.0 - 62.0 Hz |
IEC 1212-2 6.2 |
| <= 5.5 @Frequency 1.00e+6 Hz |
<= 5.5 @Frequency 1.00e+6 Hz |
IEC 1212-2 6.2 | |
| Dielectric Breakdown | >= 35000 V @Temperature 90.0 °C |
>= 35000 V @Temperature 194 °F |
In oil, parallel to laminations; IEC 1212-2 6.2 |
| Dissipation Factor | <= 0.050 @Frequency 48.0 - 62.0 Hz |
<= 0.050 @Frequency 48.0 - 62.0 Hz |
IEC 1212-2 6.2 |
| <= 0.050 @Frequency 1.00e+6 Hz |
<= 0.050 @Frequency 1.00e+6 Hz |
IEC 1212-2 6.2 | |
| Comparative Tracking Index | >= 180 V | >= 180 V | IEC 1212-2 6.4 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Thermal Endurance | 155 T.I. | IEC 1212-2 7.1 |
| Water Absorption | < 40 mg | IEC 1212-2 8.2; Test piece 50 x 50 x 10 mm |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8961 (UF) Synthetic Oil
- Techmer ES Plastiblend® PA6 SF80 L
- Borealis BE50-7032 Polypropylene Homopolymer for Non-Pressure pipes and extruded sheets
- Polyram RamLloy PB917G6 Nylon 6/Polypropylene Alloy, 30% Glass Fiber Reinforced
- DuPont Performance Polymers Hytrel® HTR8341C BK320 Polyester Elastomer TPC-ET (Unverified Data**)
- Aaron Industries AAROPRENE® TFIPP 2030 High Impact Talc Filled Polypropylene
- A. Schulman ComAlloy Comtuf® 152 Polypropylene, Mineral Reinforced, Impact Modified
- Polyram Polytron A40B01 Nylon 66, 40% Long Fiber
- DuPont Elvax® 3173SHB Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion, Blown Film (discontinued **)<
Copyright © lookpolymers.com All Rights Reserved