Hexcel® HexPly® M48 180°C/356°F Curing Epoxy Matrix, M48/42%/G1094/1000

Category Polymer , Thermoset , Epoxy , Epoxy Cure Resin
Manufacturer Hexcel
Trade Name HexPly®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® M48 180°C/356°F Curing Epoxy Matrix, M48/42%/G1094/1000.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Fiber: T800H 6K, 5H Satin weave, 290 g/m2Information provided by HexCel
Physical Properties Metric English Comments
Density 1.28 g/cc
0.0462 lb/in³
Resin
1.54 g/cc
0.0556 lb/in³
Nominal Laminate
1.81 g/cc
0.0654 lb/in³
Fibre
Mechanical Properties Metric English Comments
Tensile Strength, Yield 991 MPa

@Temperature 23.0 °C
 144000 psi

@Temperature 73.4 °F
 prEN2561 Type B
Tensile Modulus 67.0 GPa

@Temperature 23.0 °C
 9720 ksi

@Temperature 73.4 °F
 prEN2561 Type B
Compressive Yield Strength 282 MPa

@Temperature 23.0 °C
 40900 psi

@Temperature 73.4 °F
 Compression After Impact @ 6.7 J/mm; AITM 1.0010
650 MPa

@Temperature 23.0 °C
 94300 psi

@Temperature 73.4 °F
 prEN2580 Type B
Compressive Modulus 59.0 GPa

@Temperature 23.0 °C
 8560 ksi

@Temperature 73.4 °F
 prEN2580 Type B
Shear Modulus 4.70 GPa

@Temperature 23.0 °C
 682 ksi

@Temperature 73.4 °F
 In-Plane; prEN6032
Shear Strength 76.4 MPa

@Temperature 23.0 °C
 11100 psi

@Temperature 73.4 °F
 ILSS; prEN2563
116 MPa

@Temperature 23.0 °C
 16800 psi

@Temperature 73.4 °F
 In-Plane; prEN6032
Thermal Properties Metric English Comments
Glass Transition Temp, Tg 201 °C
394 °F
Onset
218 °C
424 °F
Peak
Processing Properties Metric English Comments
Shelf Life 12.0 Month

@Temperature -18.0 °C
 12.0 Month

@Temperature -0.400 °F
Descriptive Properties Value Comments
Cured Thickness per Ply (cm) 0.0324
Fiber Volume (%) 49.4
Tack Life (days) 15