Hexcel® HexPly® M36 180°C (350°F) Curing Epoxy Matrix, Unidirectional Prepreg Laminate (M36/32%/135/HTA)

Category Polymer , Thermoset , Epoxy , Epoxy Cure Resin
Manufacturer Hexcel
Trade Name HexPly®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® M36 180°C (350°F) Curing Epoxy Matrix, Unidirectional Prepreg Laminate (M36/32%/135/HTA).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Tenax HTA fiberInformation provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 365 MPa
52900 psi
Open Hole Tension, Hot/Wet
384 MPa

@Temperature 23.0 °C
 55700 psi

@Temperature 73.4 °F
 Open Hole Tension
2143 MPa

@Temperature 23.0 °C
 310800 psi

@Temperature 73.4 °F
Tensile Modulus 140 GPa

@Temperature 23.0 °C
 20300 ksi

@Temperature 73.4 °F
Compressive Yield Strength 204 MPa
29600 psi
Compression After Impact, 30J
205 MPa
29700 psi
Compression After Impact, 40J
243 MPa
35200 psi
Compression After Impact, 20J
251 MPa
36400 psi
Open Hole Compression, Hot/Wet
278 MPa
40300 psi
Compression After Impact, 10J
273 MPa

@Temperature 23.0 °C
 39600 psi

@Temperature 73.4 °F
 Open Hole Compression
Processing Properties Metric English Comments
Shelf Life >= 12.0 Month

@Temperature -18.0 °C
 >= 12.0 Month

@Temperature -0.400 °F