Braskem LH118 Blown Film Extrusion Linear Low Density Polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | Braskem |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Braskem LH118 Blown Film Extrusion Linear Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Stretch films; Liners; LDPE and HDPE blends; Packages for general use.Information provided by Braskem.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.916 g/cc | 0.916 g/cc | ASTM D1505/D792 |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 1080 % | 1080 % | ASTM D882 |
| Film Elongation at Break, TD | 1360 % | 1360 % | ASTM D882 |
| Elmendorf Tear Strength MD | 300 g | 300 g | gF; ASTM D1922 |
| Elmendorf Tear Strength TD | 510 g | 510 g | gF; ASTM D1922 |
| Dart Drop Test | 150 g | 0.331 lb | gF/50%f; ASTM D1709 |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 40.0 MPa | 5800 psi | ASTM D882 |
| 1% Secant Modulus, MD | 200 MPa | 29000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 210 MPa | 30500 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 24 % @Thickness 0.0250 mm |
24 % @Thickness 0.000984 in |
ASTM D1003 |
| Gloss | 69 % @Thickness 0.0250 mm |
69 % @Thickness 0.000984 in |
60°; ASTM D2457 |
Users viewing this material also viewed the following:
- Polikim ULPOLEN® 1000 UHMWPE, UV, Antistatic
- Polykemi AB SCANMID 6 B12^ FC Nylon 6
- LG Chemical LUCEL N109-02 General Purpose POM, Unreinforced, Externally Lubricated, Standard Viscosity
- Materion BrushCAST® 21C High Strength Casting Alloy (As Cast & Aged)
- American Elements Silicon Nanoparticles
- A. Schulman POLYBATCH™ FTA-50-P Concentrate Based In LLDPE
- CoorsTek Reaction Bonded Silicon Carbide, SCRB (SC-2)
- CLAL-MSX ARCAP Anticorrosion AP4 H12 1/2 hard, Rolled Copper Alloy
- California Fine Wire Nickel 211 (Nickel Manganese Alloy)
- ATI Allvac® M-50 Specialty Steel, Heat Treatment: 1107°C (2025°F) Q+T
Copyright © lookpolymers.com All Rights Reserved