Hexcel® HexPly® 8552 Epoxy Matrix, IM7 Fiber

Category Polymer , Thermoset , Epoxy , Epoxy Cure Resin
Manufacturer Hexcel
Trade Name HexPly®
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Hexcel® HexPly® 8552 Epoxy Matrix, IM7 Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Information provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 91.7 MPa
<br>@Temperature 104 °C
 13300 psi
<br>@Temperature 220 °F
 90°, Dry
111 MPa
<br>@Temperature 25.0 °C
 16100 psi
<br>@Temperature 77.0 °F
 90°, Dry
174 MPa
<br>@Temperature -55.0 °C
 25300 psi
<br>@Temperature -67.0 °F
 90°, Dry
428 MPa
<br>@Temperature 25.0 °C
 62100 psi
<br>@Temperature 77.0 °F
 Open Hole Tensile, Dry
2540 MPa
<br>@Temperature 104 °C
 368000 psi
<br>@Temperature 220 °F
 0°, Dry
2570 MPa
<br>@Temperature -55.0 °C
 373000 psi
<br>@Temperature -67.0 °F
 0°, Dry
2720 MPa
<br>@Temperature 25.0 °C
 395000 psi
<br>@Temperature 77.0 °F
 0°, Dry
Tensile Modulus 10.3 GPa
<br>@Temperature 220 °C
 1500 ksi
<br>@Temperature 428 °F
 90°, Dry
11.7 GPa
<br>@Temperature 77.0 °C
 1700 ksi
<br>@Temperature 171 °F
 90°, Dry
19.3 GPa
<br>@Temperature -67.0 °C
 2800 ksi
<br>@Temperature -88.6 °F
 90°, Dry
163 GPa
<br>@Temperature -67.0 °C
 23700 ksi
<br>@Temperature -88.6 °F
 0°, Dry
163 GPa
<br>@Temperature 220 °C
 23700 ksi
<br>@Temperature 428 °F
 0°, Dry
164 GPa
<br>@Temperature 77.0 °C
 23800 ksi
<br>@Temperature 171 °F
 0°, Dry
Flexural Yield Strength 1860 MPa
<br>@Temperature 25.0 °C
 270000 psi
<br>@Temperature 77.0 °F
 0°, Dry
Flexural Modulus 15.2 GPa
<br>@Temperature 25.0 °C
 2200 ksi
<br>@Temperature 77.0 °F
 0°, Dry
Compressive Yield Strength 170 MPa
<br>@Temperature 82.2 °C
 24600 psi
<br>@Temperature 180 °F
 0°, Wet, Fill Compression
214 MPa
<br>@Temperature 25.0 °C
 31000 psi
<br>@Temperature 77.0 °F
 Compression After Impact, Dry
226 MPa
<br>@Temperature 104 °C
 32800 psi
<br>@Temperature 220 °F
 0°, Dry, Fill Compression
234 MPa
<br>@Temperature 25.0 °C
 34000 psi
<br>@Temperature 77.0 °F
 After 1500 in-in-lb/in impact, Dry
236 MPa
<br>@Temperature 25.0 °C
 34200 psi
<br>@Temperature 77.0 °F
 0°, Wet, Fill Compression
305 MPa
<br>@Temperature 25.0 °C
 44200 psi
<br>@Temperature 77.0 °F
 0°, Dry, Fill Compression
336 MPa
<br>@Temperature 25.6 °C
 48800 psi
<br>@Temperature 78.0 °F
 Open Hole Compression, Dry
1480 MPa
<br>@Temperature 90.6 °C
 215000 psi
<br>@Temperature 195 °F
 0°, Dry
1690 MPa
<br>@Temperature 25.0 °C
 245000 psi
<br>@Temperature 77.0 °F
 0°, Dry
Compressive Modulus 150 GPa
<br>@Temperature 25.0 °C
 21700 ksi
<br>@Temperature 77.0 °F
 0°, Dry
162 GPa
<br>@Temperature 90.6 °C
 23500 ksi
<br>@Temperature 195 °F
 0°, Dry
Shear Strength 80.0 MPa
<br>@Temperature 82.2 °C
 11600 psi
<br>@Temperature 180 °F
 0° Short Beam, Wet
93.8 MPa
<br>@Temperature 104 °C
 13600 psi
<br>@Temperature 220 °F
 0° Short Beam, Dry
106 MPa
<br>@Temperature 104 °C
 15400 psi
<br>@Temperature 220 °F
 +/- 45° In-Plane, Dry
115 MPa
<br>@Temperature 25.0 °C
 16700 psi
<br>@Temperature 77.0 °F
 0° Short Beam, Wet
120 MPa
<br>@Temperature 25.0 °C
 17400 psi
<br>@Temperature 77.0 °F
 +/- 45° In-Plane, Dry
137 MPa
<br>@Temperature 25.0 °C
 19900 psi
<br>@Temperature 77.0 °F
 0° Short Beam, Dry
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 121 °C
250 °F
Epoxy Matrix Limit