Hexcel® HexPly® 8552 Epoxy Matrix, A280-5H Fiber

Category Polymer , Thermoset , Epoxy , Epoxy Cure Resin
Manufacturer Hexcel
Trade Name HexPly®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® 8552 Epoxy Matrix, A280-5H Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 352 MPa

@Temperature 25.0 °C
 51000 psi

@Temperature 77.0 °F
 Open Hole Tensile, Dry
752 MPa

@Temperature -55.0 °C
 109000 psi

@Temperature -67.0 °F
 90°, Dry
772 MPa

@Temperature 93.3 °C
 112000 psi

@Temperature 200 °F
 90°, Dry
800 MPa

@Temperature 25.0 °C
 116000 psi

@Temperature 77.0 °F
 90°, Dry
827 MPa

@Temperature -55.0 °C
 120000 psi

@Temperature -67.0 °F
 0°, Dry
876 MPa

@Temperature 25.0 °C
 127000 psi

@Temperature 77.0 °F
 0°, Dry
903 MPa

@Temperature 90.6 °C
 131000 psi

@Temperature 195 °F
 0°, Dry
Tensile Modulus 64.8 GPa

@Temperature 200 °C
 9400 ksi

@Temperature 392 °F
 90°, Dry
65.5 GPa

@Temperature 77.0 °C
 9500 ksi

@Temperature 171 °F
 90°, Dry
66.9 GPa

@Temperature -67.0 °C
 9700 ksi

@Temperature -88.6 °F
 90°, Dry
66.9 GPa

@Temperature 77.0 °C
 9700 ksi

@Temperature 171 °F
 0°, Dry
68.9 GPa

@Temperature 195 °C
 10000 ksi

@Temperature 383 °F
 0°, Dry
70.3 GPa

@Temperature -67.0 °C
 10200 ksi

@Temperature -88.6 °F
 0°, Dry
Flexural Yield Strength 1030 MPa

@Temperature 25.0 °C
 150000 psi

@Temperature 77.0 °F
 0°, Dry
Flexural Modulus 58.6 GPa

@Temperature 25.0 °C
 8500 ksi

@Temperature 77.0 °F
 0°, Dry
Compressive Yield Strength 281 MPa

@Temperature 25.0 °C
 40800 psi

@Temperature 77.0 °F
 Compression After Impact, Dry
370 MPa

@Temperature 25.6 °C
 53700 psi

@Temperature 78.0 °F
 Open Hole Compression, Dry
510 MPa

@Temperature 93.3 °C
 74000 psi

@Temperature 200 °F
 0°, Wet
526 MPa

@Temperature 25.0 °C
 76300 psi

@Temperature 77.0 °F
 Compression Before Impact, Dry
752 MPa

@Temperature 93.3 °C
 109000 psi

@Temperature 200 °F
 0°, Dry
889 MPa

@Temperature 25.0 °C
 129000 psi

@Temperature 77.0 °F
 0°, Dry, Fill Compression
924 MPa

@Temperature 25.0 °C
 134000 psi

@Temperature 77.0 °F
 0°, Dry
1030 MPa

@Temperature -55.0 °C
 150000 psi

@Temperature -67.0 °F
 0°, Dry, Fill Compression
Compressive Modulus 64.1 GPa

@Temperature 25.0 °C
 9300 ksi

@Temperature 77.0 °F
 0°, Dry
66.9 GPa

@Temperature 93.3 °C
 9700 ksi

@Temperature 200 °F
 0°, Dry
Shear Strength 47.6 MPa

@Temperature 93.3 °C
 6900 psi

@Temperature 200 °F
 0° Short Beam, Dry
68.9 MPa

@Temperature 25.0 °C
 10000 psi

@Temperature 77.0 °F
 0° Short Beam, Wet
78.6 MPa

@Temperature 25.0 °C
 11400 psi

@Temperature 77.0 °F
 0° Short Beam, Dry
80.7 MPa

@Temperature 25.0 °C
 11700 psi

@Temperature 77.0 °F
 Fill Short Beam, Dry
94.5 MPa

@Temperature -55.0 °C
 13700 psi

@Temperature -67.0 °F
 Fill Short Beam, Dry
110 MPa

@Temperature 25.0 °C
 15900 psi

@Temperature 77.0 °F
 +/- 45° In-Plane, Dry
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 121 °C
250 °F
Epoxy Matrix Limit