- H.C. Starck Amperit® 559.074 Agglomerated, Sintered Tungsten Carbide-Cobalt-Chromium 86-6-8 (WC-Co-Cr)
H.C. Starck Amperit® 559.074 Agglomerated, Sintered Tungsten Carbide-Cobalt-Chromium 86-6-8 (WC-Co-Cr)
| Category | Ceramic , Carbide |
| Manufacturer | H.C. Starck |
| Trade Name | Amperit® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | H.C. Starck Amperit® 559.074 Agglomerated, Sintered Tungsten Carbide-Cobalt-Chromium 86-6-8 (WC-Co-Cr).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 4.80 - 5.80 g/cc | 0.173 - 0.210 lb/in³ | ASTM B212 |
| Particle Size | 16 - 20 µm | 16 - 20 µm | 10% |
| 28 - 34 µm | 28 - 34 µm | 50% | |
| 50 - 60 µm | 50 - 60 µm | 90% | |
| 88 µm | 88 µm | 100% less than |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 5.2 - 5.8 % | 5.2 - 5.8 % | |
| Chromium, Cr | 7.0 - 9.0 % | 7.0 - 9.0 % | |
| Cobalt, Co | 5.0 - 7.0 % | 5.0 - 7.0 % | |
| Iron, Fe | <= 0.30 % | <= 0.30 % | |
| Oxygen, O | <= 0.20 % | <= 0.20 % | |
| Tungsten, W | 77.7 - 82.8 % | 77.7 - 82.8 % |
Users viewing this material also viewed the following:
- Omya OMYACARB® 8 - LU Calcium Carbonate
- Kinlead HSD13 Normal Grade Heat Sealable Film (thickness: 18 µm)
- Kraton® G1641 H (SEBS) Linear Triblock Copolymer
- Indium Corp. Indalloy 101 Bismuth-Lead-Tin Solder Alloy
- Mueller Ecostreamâ„¢ C36300 Copper Zinc Lead Alloy
- Schott GG435 Long Pass Filter
- ExxonMobil Optema® TC-110 Blown Ethylene Methyl Acrylate
- Arlon 61089R040 0.040" (1.02 mm) Uncured/Cured Silicone Rubber with Denier Vectran HS Substrate
- Asahi Kasei Xyron® X9653 Modified Polyphenylene Ether
- ArcelorMittal 16 High formability steel for drawing, Hot rolled
Copyright © lookpolymers.com All Rights Reserved