Gwent Electronic Materials C2090210P12 Silver Ink

Category	Fluid , Other Engineering Material , Ceramic/Metallic Coating , Polymer , Thermoplastic , Adhesives, Sealants, and Coatings
Manufacturer	Gwent Electronic Materials Ltd.
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Gwent Electronic Materials C2090210P12 Silver Ink.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This product is part of a range of Heat Curable Inks designed specifically for use in Electro Luminescent systems. These products are based on a unique curing process that results in the low temperature formation of a thermosetting polymer. This ink has excellent adhesion, chemical and environmental resistance properties. Excellent adhesion to ITO, chemical and environmental resistance. Screen Printing Equipment: semi-automatic, manualScreen Types: stainless steel, polyester, mesh 156-325tpiSubstrate: ITO coated polyesterInformation provided by Gwent Electronic Materials Ltd.

Physical Properties	Metric	English	Comments
Solids Content	57 - 59.75 % @Temperature 700 °C	57 - 59.75 % @Temperature 1290 °F
Viscosity	6500 - 8500 cP @Shear Rate 230 1/s, Temperature 25.0 °C	6500 - 8500 cP @Shear Rate 230 1/s, Temperature 77.0 °F	Haake VT 550 PK1.1°
Thickness	10.0 microns	0.394 mil	Cured Film Thickness on 175µm ITO coated polyester
Storage Temperature	20.0 °C	68.0 °F	sealed container

Electrical Properties	Metric	English	Comments
Surface Resistivity per Square	0.20 ohm @Thickness 0.0250 mm	0.20 ohm @Thickness 0.000984 in	Normalized, Printed on PET Film

Processing Properties	Metric	English	Comments
Cure Time	3.00 min @Temperature 130 °C	0.0500 hour @Temperature 266 °F	belt dryer
	10.0 min @Temperature 130 °C	0.167 hour @Temperature 266 °F	box oven
Shelf Life	6.00 Month	6.00 Month

Descriptive Properties	Value	Comments
Coverage cm2/g	165	Using a 230 mesh stainless steel screen