Gwent Electronic Materials C2030922D1 Silver Ink

Category	Fluid , Metal , Other Engineering Material , Ceramic/Metallic Coating
Manufacturer	Gwent Electronic Materials Ltd.
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Gwent Electronic Materials C2030922D1 Silver Ink.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Silver Ink C2030922D1 is a grey ink with a pine smell at a ready to use viscosity suitable for firing on glass and ceramic to form conductive tracks. The ink should be gently stirred before use avoiding introduction of air bubbles.Silver Ink has a low resistance ink designed for use as the heating bars and tracks on automobile backlights and other circuits on glass. It has a dark back color when printed and fired on float side of glass. It can be printed onto IR or UV black enamels. Screen Printing Equipment: semi-automatic, automaticScreen Types: stainless steel, polyester, mesh 156-325 tpiSubstrate: GlassInformation provided by Gwent Electronic Materials Ltd.

Physical Properties	Metric	English	Comments
Solids Content	84 - 86 % @Temperature 700 Â°C	84 - 86 % @Temperature 1290 Â°F
Viscosity	3000 - 5500 cP @Shear Rate 230 1/s, Temperature 25.0 Â°C	3000 - 5500 cP @Shear Rate 230 1/s, Temperature 77.0 Â°F	Haake VT 550 PK1.1Â°
Storage Temperature	20.0 Â°C	68.0 Â°F	sealed container

Electrical Properties	Metric	English	Comments
Surface Resistivity per Square	0.015 - 0.020 ohm @Thickness 0.0250 mm	0.015 - 0.020 ohm @Thickness 0.000984 in	Printed onto 125Âµm PET film
	0.030 - 0.045 ohm @Thickness 0.0100 mm	0.030 - 0.045 ohm @Thickness 0.000394 in	Printed onto 125Âµm PET film

Processing Properties	Metric	English
Sintering Temperature	550 - 750 Â°C	1020 - 1380 Â°F
Cure Time	15.0 min @Temperature 150 Â°C	0.250 hour @Temperature 302 Â°F
Shelf Life	6.00 Month	6.00 Month

Descriptive Properties	Value	Comments
Bending Test	Ink survived 3 cycles	Printed onto 125Âµm PET film, Failure at resistance 10 times the initial value using 2kg weight.
Coverage cm2/g	110	Using a 230 mesh stainless steel screen
Double Curing	Aging factor of -0.7% after double curing at 150C for 15 mins.	Printed onto 125Âµm PET film
Hot Water Test	Aging factor of -0.2% after boiling for 1 hr.	Printed onto 125Âµm PET film