- Glastic Laminates/Shapes UTR Glass-Mat-Reinforced, Mineral Filled Polyester Laminate
Glastic Laminates/Shapes UTR Glass-Mat-Reinforced, Mineral Filled Polyester Laminate
| Category | Polymer , Thermoset , Filled/Reinforced Thermoset , Polyester, TS |
| Manufacturer | Glastic |
| Trade Name | Laminates/Shapes |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Glastic Laminates/Shapes UTR Glass-Mat-Reinforced, Mineral Filled Polyester Laminate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Glastic Corporation.NEMA GPO-3/GPO-3P. Developed for transit industry where smoke generation and toxicity are of primary concern.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.81 g/cc | 0.0654 lb/in³ | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 54.0 MPa | 7830 psi | ASTM D638 |
| Tensile Modulus | 12.0 GPa | 1740 ksi | ASTM D638 |
| Flexural Strength | 152 MPa | 22000 psi | ASTM D790 |
| Compressive Strength | 228 MPa | 33100 psi | ASTM D695 |
| Shear Strength | 80.0 MPa | 11600 psi | ASTM D732 |
| Izod Impact, Notched | 4.80 J/cm | 8.99 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 20.0 µm/m-°C @Temperature 20.0 °C |
11.1 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Thermal Conductivity | 0.270 W/m-K | 1.87 BTU-in/hr-ft²-°F | ASTM C177 |
| Maximum Service Temperature, Air | 155 °C | 311 °F | NEMA temperature |
| UL RTI, Electrical | 130 °C | 266 °F | UL 746B |
| UL RTI, Mechanical with Impact | 160 °C | 320 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness >=0.800 mm |
V-0 @Thickness >=0.0315 in |
UL94 |
| Oxygen Index | 35 % | 35 % | ASTM D2862 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 3.10e+12 ohm | 3.10e+12 ohm | Insulation Resistance, ASTM D257 |
| Dielectric Constant | 4.1 @Frequency 60 Hz |
4.1 @Frequency 60 Hz |
ASTM D150 |
| 4.1 @Frequency 1e+6 Hz |
4.1 @Frequency 1e+6 Hz |
ASTM D150 | |
| Dielectric Strength | 18.0 kV/mm | 457 kV/in | Perpendicular, Short-term, in air; ASTM D149 |
| Dissipation Factor | 0.010 @Frequency 1e+6 Hz |
0.010 @Frequency 1e+6 Hz |
ASTM D150 |
| 0.013 @Frequency 60 Hz |
0.013 @Frequency 60 Hz |
ASTM D150 | |
| Arc Resistance | 180 sec | 180 sec | ASTM D495 |
| Comparative Tracking Index | >= 500 V | >= 500 V | UL746A |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 mm/min | 0.000 in/min | UL746A |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 4008 RC Medium Impact 40% Glass Filled Polypropylene
- Solvay Specialty Polymers Halar® 500 ECTFE Fluoropolymer (discontinued **)
- Global F-8000 High Density Polyethylene
- Global TPO-55D TPO Grade
- SABIC Innovative Plastics ULTEM 1010FC PEI (Europe-Africa-Middle East)
- Eastman Tenite 380A4000015 Cellulose Acetate Propionate, Clear, Trsp
- CP-Polymer-Technik Wellamid® 6600 MZ 315 CP Combination Nylon 66, Dry
- DuPont™ Appeel® 11D888 Ethylene Vinyl Acetate
- Aquabond Technologies Aquabond™ ABS-65 Water Soluble Adhesive and Bonding Thermoplastic
- DuPont Performance Polymers VTR 8500 (GLT-S) 8500 Peroxide Cured Fluoroelastomer (FKM) Formulation (discontin
Copyright © lookpolymers.com All Rights Reserved