Garlock GYLONÂ® 3545 Layered Microcellular PTFE Gasketing

Category	Polymer , Thermoplastic , Fluoropolymer , PTFE
Manufacturer	Garlock Rubber Technologies
Trade Name	GYLON®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Garlock GYLONÂ® 3545 Layered Microcellular PTFE Gasketing.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Microcellular PTFE gasket with rigid PTFE coreHighly compressible PTFE outer layers seal under low bolt load- suitable for many non-metallic flangesCompressible layers conform to surface irregularities, especially on warped, pitted or scratched flangesRigid PTFE core reduces cold flow and creep normally associated with conventional PTFE gasketsMedia: Strong caustics, strong acids, hydrocarbons, chlorine and cryogenics.Conforms to FDA regulations.Information provided by Garlock Rubber Technologies

Physical Properties	Metric	English	Comments
Density	2.05 g/cc	0.0741 lb/inÂ³	estimated by MatWeb
Permeability	0.015	0.015	Gas Permeability, cc/min; DIN 3535 Part 4

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	260 Â°C @Pressure 8.27 MPa	500 Â°F @Pressure 1200 psi	Continuous
Minimum Service Temperature, Air	-268 Â°C	-450 Â°F

Electrical Properties	Metric	English	Comments
Dielectric Strength	9.61 kV/mm @Temperature 121 Â°C, Time 10800 sec	244 kV/in @Temperature 250 Â°F, Time 3.00 hour	0.125 in. thickness; ASTM D149
	9.76 kV/mm @Temperature 121 Â°C, Time 10800 sec	248 kV/in @Temperature 250 Â°F, Time 3.00 hour	0.0625 in. thickness; ASTM D149
	8.74 kV/mm @Thickness 1.59 mm	222 kV/in @Thickness 0.0625 in	100% RH for 96 hours; ASTM D149
	10.4 kV/mm @Thickness 3.17 mm	264 kV/in @Thickness 0.125 in	100% RH for 96 hours; ASTM D149

Compliance Properties	Metric	English	Comments
FDA	Yes	Yes

Descriptive Properties	Value	Comments
Color	White
Compressibility, %	70-85	ASTM F36
Creep Relaxation, %	10	ASTM F38
Sealability ASTM F37B, ml/hr	0.15	ASTM Fuel A

Users viewing this material also viewed the following: