Freudenberg Simrit S50 Silicone Elastomer (VMQ)
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone |
| Manufacturer | Freudenberg Simrit |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Freudenberg Simrit S50 Silicone Elastomer (VMQ).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General Purpose; AMS 3301; A-A-59588 (ZZ-R-765) Class 2A, 2B Grade 40; Good heat resistance. Poor resistance to abrasion, tear and cut growth; low tensile strength; inferior resistance to oil, gasoline and solvents; poor resistance to alkalis and acids.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | Original Properties; ASTM D297 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 50 | 50 | Original Properties; ASTM D2240 |
| 42 @Temperature 150 °C |
42 @Temperature 302 °F |
ASTM #1 Oil Immersion for 70 hours; ASTM D2240 | |
| 56 @Temperature 225 °C |
56 @Temperature 437 °F |
Air Aging, 70 hours; ASTM D2240 | |
| Tensile Strength, Ultimate | 6.55 MPa | 950 psi | Original Properties; ASTM D412 Die C |
| 5.830 MPa @Temperature 150 °C |
845.5 psi @Temperature 302 °F |
ASTM #1 Oil Immersion for 70 hours; ASTM D412 Die C | |
| 6.16 MPa @Temperature 225 °C |
893 psi @Temperature 437 °F |
Air Aging, 70 hours; ASTM D412 Die C | |
| Elongation at Break | 425 % | 425 % | Original Properties; ASTM D412 Die C |
| 306 % @Temperature 225 °C |
306 % @Temperature 437 °F |
Air Aging, 70 hours; ASTM D412 Die C | |
| 391 % @Temperature 150 °C |
391 % @Temperature 302 °F |
ASTM #1 Oil Immersion for 70 hours; ASTM D412 Die C | |
| 100% Modulus | 0.00155 GPa | 0.225 ksi | Original Properties; ASTM D412 Die C |
| Tear Strength | 17.7 kN/m | 101 pli | ASTM D624 Die B |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Bend (flat) | Pass | Air Aging for 70 hours at 225°C |
| Color | Red | |
| Decomposition per AMS 3302G | None | |
| Low Temperature Brittleness | Pass, No cracks | ASTM D2137 |
| Surface Tackiness per AMS 3302G | None | |
| Volume Change (%), ASTM D471 | 7 | ASTM #1 Oil Immersion for 70 hours at 150°C |
Users viewing this material also viewed the following:
- Nylene® 402 Nylon 6
- PolyOne Geon™ Vinyl Flexible XV3432 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Karina 75/204-D-AT-IS-H Clear PVC Compound
- LG Chemical LUPOL SO-5202P High Impact Polypropylene, 20% Polymer Alloy
- Wellman Wellamid® GF33-66 XE-NBK1 33% Glass Fiber Reinforced, Engineering Grade Nylon 66
- CMW® ELKONIUM 30 pure platinum
- Zhejiang Juner PC-A1-1 Top-Grade Flame Retardant UV-Resistant
- Fainplast Compounds MGS 79 Medical Flexible PVC, Injection Molding
- Addiplast Addinyl B2 V30 Nylon 6, 30% Glass Filled
Copyright © lookpolymers.com All Rights Reserved