Freudenberg Simrit S315 Silicone Elastomer (VMQ)
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone |
| Manufacturer | Freudenberg Simrit |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Freudenberg Simrit S315 Silicone Elastomer (VMQ).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General Purpose; AMS 3301; A-A-59588 (ZZ-R-765) Class 2A, 2B Grade 40; Good heat resistance. Poor resistance to abrasion, tear and cut growth; low tensile strength; inferior resistance to oil, gasoline and solvents; poor resistance to alkalis and acids.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | Original Properties; ASTM D297 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 75 | 75 | Original Properties; ASTM D2240 |
| 70 @Temperature 175 °C |
70 @Temperature 347 °F |
ASTM #1 Oil Immersion for 70 hours; ASTM D2240 | |
| 72 @Temperature 250 °C |
72 @Temperature 482 °F |
Polymer Reversion for 6 hours; ASTM D2240 | |
| 79 @Temperature 250 °C |
79 @Temperature 482 °F |
Air Aging, 70 hours; ASTM D2240 | |
| Tensile Strength, Ultimate | 8.219 MPa | 1192 psi | Original Properties; ASTM D1414 |
| 6.904 MPa @Temperature 250 °C |
1001 psi @Temperature 482 °F |
Air Aging, 70 hours; ASTM D1414 | |
| 7.068 MPa @Temperature 175 °C |
1025 psi @Temperature 347 °F |
ASTM #1 Oil Immersion for 70 hours; ASTM D1414 | |
| Elongation at Break | 204 % | 204 % | Original Properties; ASTM D1414 |
| 146.88 % @Temperature 250 °C |
146.88 % @Temperature 482 °F |
Air Aging, 70 hours; ASTM D1414 | |
| 181.56 % @Temperature 175 °C |
181.56 % @Temperature 347 °F |
ASTM #1 Oil Immersion for 70 hours; ASTM D1414 | |
| Compression Set | 16.2 % @Temperature 225 °C, Time 79200 sec |
16.2 % @Temperature 437 °F, Time 22.0 hour |
60 max, over 0.11 inch cross section; ASTM D395 |
| 17.3 % @Temperature 225 °C, Time 79200 sec |
17.3 % @Temperature 437 °F, Time 22.0 hour |
70 max, under .11 inch cross section; ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Minimum Service Temperature, Air | -45.6 °C | -50.0 °F | Retraction Temperature, TR10; ASTM D1329 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Red | |
| Volume Change (%), ASTM D471 | 5.4 | ASTM #1 Oil Immersion for 70 hours at 302°F |
Users viewing this material also viewed the following:
- Pau Tai UNISTAB BT-11 Organo Tin Stabilizer
- Akro-Plastic Akromid® S31 (3484) PA 6.10 Dry (discontinued **)
- Momentive Performance Materials AC6003 Boron Nitride (BN) Powder
- Lucite International Colacryl ® TS2082 Acrylic Resin
- Gouda Vuurvast CURAS 50 D Moldable Refractory Material
- SABIC Innovative Plastics Valox® 420 PBT
- ExxonMobil 629 Mobilgear 600 Series
- SABIC Innovative Plastics Xylex X7529OQ PC+POLYESTER (Asia Pacific)
- Lucent Polymers TPP-220 Polypropylene, 20% Talc Filled, Impact Modified
- Covestro Bayblend® SF 1443 Polycarbonate + ABS Blend Structural Foam (discontinued **)
Copyright © lookpolymers.com All Rights Reserved