Formosa Plastics Formolene® HF3728 Film (Hexene) HDPE

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer	Formosa Plastics Corporation, USA
Trade Name	Formolene®
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Formosa Plastics Formolene® HF3728 Film (Hexene) HDPE.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

High Density Polyethylene Medium Molecular weight Film Resin Formolene® HF3728 is a medium density resin that provides an excellent overall balance of tensile, impact, and tear properties in thin film. Processing performance is excellent on high stalk lines. Formolene® HF3728 meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact.Applications: Trash Can Liners, Produce and MerchandiseInformation provided by Formosa Plastics Corporation, USA

Physical Properties	Metric	English	Comments
Density	0.937 g/cc	0.0339 lb/in³	ASTM D1505
Melt Flow	0.30 g/10 min <br>@Load 2.16 kg,<br> Temperature 190 °C	0.30 g/10 min <br>@Load 4.76 lb,<br> Temperature 374 °F	ASTM D1238
High Load Melt Index	20 g/10 min <br>@Load 21.6 kg,<br> Temperature 190 °C	20 g/10 min <br>@Load 47.6 lb,<br> Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	21.4 MPa	3100 psi	2" (50mm) per min; ASTM D882
Film Tensile Strength at Yield, TD	21.4 MPa	3100 psi	2" (50mm) per min; ASTM D882
Film Elongation at Break, MD	500 %	500 %	2" (50mm) per min; ASTM D882
Film Elongation at Break, TD	600 %	600 %	2" (50mm) per min; ASTM D882
Elmendorf Tear Strength MD	50 g	50 g	ASTM D1922
Elmendorf Tear Strength TD	500 g	500 g	ASTM D1922
Dart Drop Test	130 g <br>@Thickness 660 mm	0.287 lb <br>@Thickness 26.0 in	ASTM D1709
Film Tensile Strength at Break, MD	42.1 MPa	6100 psi	2" (50mm) per min; ASTM D882
Film Tensile Strength at Break, TD	42.1 MPa	6100 psi	2" (50mm) per min; ASTM D882

Processing Properties	Metric	English	Comments
Blow-up Ratio (BUR)	4.0	4.0