Fiberfil® PP-60/TC/15/VO/ND Polypropylene Homopolymer, 15% Talc Filled, Flame Retardant
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® PP-60/TC/15/VO/ND Polypropylene Homopolymer, 15% Talc Filled, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ISO 527 |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527 |
| Flexural Strength | 37.9 MPa | 5500 psi | ISO 178 |
| Flexural Modulus | 1.65 GPa | 240 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 2.10 kJ/m² | 0.999 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 13.5 kJ/m² | 6.42 ft-lb/in² | ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Heat of Fusion | 40.0 J/g | 17.2 BTU/lb | Primary; ASTM D3418 |
| Melting Point | 162 °C | 323 °F | Primary; ASTM D3418 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
Users viewing this material also viewed the following:
- PolyOne Bergamid™ A700 TM-YF Polyamide 66 (Nylon 66)
- NOVA Chemicals Novapol® TR-0242-U MDPE Rotational Molding Resin (discontinued **)
- 3A Composites Core Materials AIREX® C51.60 Industrial Processing Foam
- MarkeTech Spinel (MgAl2O4) Single Crystal Substrate
- A. Schulman POLYBATCH™ MAS-25 Concentrate Based In LDPE
- Alliance Polymers Zythane™ 7070A Thermoplastic Polyurethane Elastomer
- Adell BR-33 Nylon 6, 15% Glass Reinforced
- 3M Novec™ 2704 Electronic Grade Coating
Copyright © lookpolymers.com All Rights Reserved