- Fiberfil® J-61/10 Polypropylene Copolymer, 10% Glass Fiber Reinforced
Fiberfil® J-61/10 Polypropylene Copolymer, 10% Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® J-61/10 Polypropylene Copolymer, 10% Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.980 g/cc | 0.980 g/cc | ASTM D792 |
| Water Absorption | 0.010 % | 0.010 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 cm/cm @Thickness 3.17 mm |
0.0040 in/in @Thickness 0.125 in |
ASTM D955 |
| 0.0050 cm/cm @Thickness 6.35 mm |
0.0050 in/in @Thickness 0.250 in |
ASTM D955 | |
| Melt Flow | 13 g/10 min | 13 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 2.07 GPa | 300 ksi | ASTM D638 |
| Flexural Strength | 51.7 MPa | 7500 psi | ASTM D790 |
| Flexural Modulus | 1.93 GPa | 280 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm @Thickness 3.17 mm |
1.20 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 305 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Permabond F202 Anaerobic Retainer
- SABIC Innovative Plastics LNP STAT-KON Noryl_HMC1010 PPE+PS
- Techmer ES Luriblend® PA6/6 CF10 TS15 BK 10% Carbon Filled
- SABIC Innovative Plastics LNP STAT-LOY PF303 PA 6
- CP-Polymer-Technik Wellamid® 6600 HWS Nylon 66, Finely Crystalline, Heat Stabilized, Dry
- DuPont Teijin Films Teijin® Tetoron® HB3 Polyester Film, 300 Gauge
- Monmouth Rubber & Plastics Superbounce 90 NEO/SBR
- LG Chemical HF-380 ABS, High Flow, High Impact
Copyright © lookpolymers.com All Rights Reserved