Fainplast Compounds HAX HFX 024-21L Halogen Free PVC
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Wire and Cable Grade |
| Manufacturer | Fainplast Compounds |
| Trade Name | HAX |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Fainplast Compounds HAX HFX 024-21L Halogen Free PVC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This product is a LSFOH silane grafted compound for cable insulation and sheating, cross-linking by heat and moisture by previous addition of a suitable catalyst masterbatch. It is highly recommended to store seperately the grafted compound and the catalyst, as prescorching may take place during the reactive extrusion.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | IEC 60811 |
| Melt Index of Compound | 3.0 g/10 min <br>@Load 21.6 kg,<br> Temperature 150 °C |
3.0 g/10 min <br>@Load 47.6 lb,<br> Temperature 302 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 45 | 45 | at 15"; IEC 60811 |
| Tensile Strength at Break | 12.5 MPa | 1810 psi | IEC 60811 |
| 13.5 MPa | 1960 psi | after crosslinking process; IEC 60811 | |
| Elongation at Break | 200 % | 200 % | after crosslinking process; IEC 60811 |
| 220 % | 220 % | IEC 60811 | |
| 0.00 % <br>@Temperature 200 °C,<br> Time 900 sec |
0.00 % <br>@Temperature 392 °F,<br> Time 0.250 hour |
permanent elongation after cooling 0.2Mpa load; IEC 60811 | |
| 5.0 % <br>@Temperature 250 °C,<br> Time 900 sec |
5.0 % <br>@Temperature 482 °F,<br> Time 0.250 hour |
permanent elongation after cooling 0.2Mpa load; IEC 60811 | |
| 20 % <br>@Temperature 200 °C,<br> Time 900 sec |
20 % <br>@Temperature 392 °F,<br> Time 0.250 hour |
elongation under 0.2Mpa load; IEC 60811 | |
| 30 % <br>@Temperature 250 °C,<br> Time 900 sec |
30 % <br>@Temperature 482 °F,<br> Time 0.250 hour |
elongation under 0.2Mpa load; IEC 60811 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Oxygen Index | 35 % | 35 % | ISO 4589 |
| Shrinkage | <= 2.0 % <br>@Temperature 100 °C,<br> Time 3600 sec |
<= 2.0 % <br>@Temperature 212 °F,<br> Time 1.00 hour |
after crosslinking process; IEC 60811 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm <br>@Temperature 20.0 °C |
1.00e+15 ohm-cm <br>@Temperature 68.0 °F |
ASTM D257 Electrodes |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 120 - 140 °C | 248 - 284 °F | |
| Zone 2 | 120 - 140 °C | 248 - 284 °F | |
| Zone 3 | 130 - 150 °C | 266 - 302 °F | |
| Zone 4 | 130 - 150 °C | 266 - 302 °F | |
| Die Temperature | 150 - 180 °C | 302 - 356 °F | |
| Head Temperature | 130 - 150 °C | 266 - 302 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Collar Temperature (°C) | 150 | |
| Emission of Halogenidric acids (%) | 0.1 | |
| Knife penetration test (%) | 50 | @ 100°C, k=1 |
| Water Absorption (mg/cm^2) | 1.5 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® DMX1214 PC Copolymer (Asia Pacific)
- ExxonMobil HD 6605.29 Injection Molding Resin (discontinued **)
- Solvay Specialty Polymers Algoflon® 55BZ+5Mos PTFE; Bronze/Molybdenum Disulphide Filled (discontinued **)
- LATI Latigloss 57 G/50 F2 PPA, 50% Glass Fiber Reinforced
- Haynes Hastelloy® C-22HS™ Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate
- SABIC Innovative Plastics LNP STAT-KON DE0029 PC (Asia Pacific)
- SK Chemicals SKYTHANE® S368D Polyester Based Thermoplastic Polyurethane Elastomer
- Teknor Apex Monprene® MP-1679L2 Thermoplastic Elastomer
- Arlon 55986C028 0.0295" Cured/Uncured Silicone Rubber with Fiberglass Substrate
- BLUESTAR 201-G25202 PBT, 25% Glass Filled
Copyright © lookpolymers.com All Rights Reserved