ExxonMobil Metallyte® 70 MET OPP Film
| Category | Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Metallyte® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Metallyte® 70 MET OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: A moderate barrier, metalized OPP film for use in adhesive and extrusion laminations to reveres-printed outer webs. The proprietary broad seal range layer offers excellent hot tack, seal integrity, and lap seal range when used with a coextruded outerweb.Availability: Latin America, North America and South AmericaKey Features:Outstanding moisture and light barriersLow MST, broad seal range, strong sealsHigh adhesion of aluminum to filmResists crazing in extrusion laminationsMET provides an excellent light barrier and a brilliant foil appearanceFeatures: In Lamination Lap SealableLight BarrierMoisture BarrierApplications:Bakery Biscuits/Cookie/CrackersCrisps and SnacksFrozen FoodIce Cream Uses: HFFS Flexible PackagingPre-made Bags – Flexible PackagingVFFS Flexible PackagingProcessing Method: Inner Web Adhesive Lamination, Inner Web Extrusion Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing, Surface Print Unsupported and Water-based Flexographic PrintingInformation provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 0.190 g/m²/day | 0.0122 g/100 in²/day | 38°C, 90% RH; ExxonMobil Method |
| Thickness | 17.8 microns | 0.700 mil | ExxonMobil Method |
| Coating Weight | 15.7 g/m² | 9.80 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 234 MPa | 34000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 4.5 % | 4.5 % | at 275°F; ExxonMobil Method |
| Shrinkage, TD | 2.5 % | 2.5 % | at 275°F; ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Optical Density | 2.4 | 2.4 | ExxonMobil Method |
| Transmission, Visible | 0.40 % | 0.40 % | ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Crimp Seal MST | 185°F | |
| Crimp Seal Strength | 450 g/in | 205°F, 20psi, 3/4sec |
| Yield | 44000 in2/lb |
Users viewing this material also viewed the following:
- LNP VALOX® SMV5845 PBT + PET Alloy, 16% Carbon Fiber Reinforcement (discontinued **)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 0.0 PHR Thanecure® ZM
- KKPC KOSYN KNB 35L Acrylonitrile Butadiene Rubber (NBR)
- Multibase Multi-ABS 3832 Natural
- Teknor Apex TruVis Esters™ DTDA Di-Tridecyl Adipate
- A. Schulman POLYBATCH™ UVK-90 UV Stabilizer Concentrate Based In Polyethylene
- China-Yixing Longly Refractories 99 Alumina Ceramic Seals
- BASF Ultramid® 82335G HS BK 102 50% Glass Filled PA6 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved