ExxonMobil Metallyte® 50 TSPM OPP Film
| Category | Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Metallyte® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Metallyte® 50 TSPM OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: A high barrier, non-sealable OPP film with one-side metalized a one-side treated. TSP< is designed for use as the inner web of a cold seal lamination or as the center web of a triplex lamination. The treated surface offers excellent cold seal compatibility.Availability: Latin America, North America and South AmericaKey Features:Outstanding light barriersImproved moisture barrierVery Good oxygen barrierExcellent cold seal adhesionAdhesive lamination capableExcellent metal adhesion and appearanceFeatures:Light BarrierMoisture BarrierOxygen BarrierApplications:Bakery Biscuits/Cookie/CrackersConfectionery, ChocolateConfectionery, Gum Confectionery, Sugar Crisps and SnacksDry Foods and Beverage PowdersPet Food Uses: HFFS Flexible PackagingPouches – Flexible PackagingVFFS Flexible PackagingProcessing Method: Cold Seal Adhesive and Inner Web Adhesive LaminationInformation provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 0.390 g/m²/day | 0.0251 g/100 in²/day | 38°C, 90% RH; ExxonMobil Method |
| Thickness | 12.7 microns | 0.500 mil | ExxonMobil Method |
| Coating Weight | 11.4 g/m² | 7.10 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Break, MD | 131 MPa | 19000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 262 MPa | 38000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 5.0 % | 5.0 % | at 275°F; ExxonMobil Method |
| Shrinkage, TD | 5.0 % | 5.0 % | at 275°F; ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Optical Density | 2.4 | 2.4 | ExxonMobil Method |
| Transmission, Visible | 0.40 % | 0.40 % | ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Wetting Tension | 0.85 receding cos theta | Matte Surface |
| Yield | 61200 in2/lb |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufTech™ GA-1038 Natural 85 PVC Compound
- Kolon Kocetal® EC701 Modified Grade Acetal Copolymer (discontinued **)
- Lehmann & Voss LUVOCOM® 1200-8493 ABS, with steel fiber
- LG Chemical LUMID SG2300B(W) PA66+GF30%, General Purpose, Good Surface
- Lucent Polymers TPP-230 Polypropylene, 30% Talc Filled, Impact Modified
- Lucobit Lucobit® 1210A Ethylene Copolymer Bitumen
- Shakespeare NX-310 diameter 0.4 mm Nylon 66 Monofilament
- Cosmic Plastics D69 Long Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound
- Westlake Hifor LT74107-F Polyethylene Film, Using Energx Technology Services (discontinued **)
Copyright © lookpolymers.com All Rights Reserved