ExxonMobil Label-Lyte™ 38DL247 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Label-Lyte™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Label-Lyte™ 38DL247 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: A super white opaque, high gloss, high yield and highly cavitated BOPP film designed for use in reel-fed wrap-around labeling applications where superior graphics are desired.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Outstanding opacity and whitenessExceptional printabilityExcellent hot melt anchorageExcellent stiffnessHigh tear and split resistanceHigh resistance to elongation on labeling machineGood mold resistanceHigh slip on untreated side of 38DL247 for optimized performance on the most demanding machines Applications:Beverage, AlcoholicBeverage, Carbonated Beverage, Mineral Waters Dairy ProductsHealth and Beauty CareHousehold and DetergentsIndustrial Uses: Reel-Fed LabelsProcessing Method: Inner Web Adhesion Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing, Surface Print Unsupported, UV Flexographic Printing and UV Offset Lithography PrintingInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | 38.1 microns | 1.50 mil | ExxonMobil Method |
| Coating Weight | 20.2 g/m² | 12.6 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 110 % | 110 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 40 % | 40 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Modulus of Elasticity | 1.20 GPa | 174 ksi | MD; ExxonMobil Method |
| 1.80 GPa | 261 ksi | TD; ExxonMobil Method | |
| Coefficient of Friction | 0.40 | 0.40 | Untreated Surface; ExxonMobil Method |
| Film Tensile Strength at Break, MD | 84.8 MPa | 12300 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 120 MPa | 17400 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 3.0 % @Temperature 135 °C, Time 432 sec |
3.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 3.0 % @Temperature 135 °C, Time 432 sec |
3.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 70 % | 70 % | 45°; ExxonMobil Method |
| Transmission, Visible | 21 % | 21 % | ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Whiteness Index | 90 | |
| Yield | 34300 in2/lb |
Users viewing this material also viewed the following:
- PolyOne Versaflex™ OM 1245X-1 Thermoplastic Elastomer (TPE)
- Stir SpA CT 60 ATC (PVC)
- Styrolution Polystyrol 168 N GR 21 PS
- Zeon Chemicals HyTemp® SC-75 Polyacrylate Curative
- DuPont™ Bynel® 50E662 Anhydride Modified Polypropylene
- DuPont Teijin Films Teijin® Tetoron® SL Polyester Film, 300 Gauge
- 3M FV173 Soft Translucent Vinyl Label Products
- EMS-Grivory Grivory® LBV-50H FWA nat PA12-GF50
- Bhansali Engineering Abstron IM17SHG PMMA- ABS Alloy
Copyright © lookpolymers.com All Rights Reserved