- ExxonMobil LLDPE LL 3404.48 Linear Low Density Polyethylene Resin
ExxonMobil LLDPE LL 3404.48 Linear Low Density Polyethylene Resin
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LLDPE |
| Manufacturer | Exxon Chemical |
| Trade Name | LLDPE |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil LLDPE LL 3404.48 Linear Low Density Polyethylene Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: LL 3404.48 is a hexane medium density polyethylene cast film grade for applications requiring high strength and high stiffness. Films produced from this resin exhibit good tensile and puncture resistance properties.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: NoProcessing Aid: No Thermal Stabilizer: YesApplications: Agricultural FilmCast FilmDiaper BacksheetOverwrap FilmInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.942 g/cc | 0.0340 lb/in³ | ExxonMobil method |
| Melt Flow | 4.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 16.5 MPa | 2400 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 17.2 MPa | 2500 psi | ASTM D882 |
| Film Elongation at Break, MD | 590 % | 590 % | ASTM D882 |
| Film Elongation at Break, TD | 830 % | 830 % | ASTM D882 |
| Puncture Energy | 0.791 J | 0.583 ft-lb | ExxonMobil Method |
| Elmendorf Tear Strength MD | 20 g | 20 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 170 g | 170 g | ASTM D1922 |
| Dart Drop Test | <= 50.0 g | <= 0.110 lb | ASTM D1709A |
| Film Tensile Strength at Break, MD | 50.3 MPa | 7300 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 34.5 MPa | 5000 psi | ASTM D882 |
| 1% Secant Modulus, MD | 379 MPa | 55000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 427 MPa | 62000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | <= 261 °C | <= 502 °F | Peak Melting Point; ExxonMobil method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 3.4 % | 3.4 % | ASTM D1003 |
| Gloss | 82 % | 82 % | 45°; ASTM D2457 |
Users viewing this material also viewed the following:
- Omni Plastics OmniTuff™ HPP CCF20 Homopolymer Polypropylene Calcium Carbonate Filled
- Global EPP PA 6C MOLY Cast Polyamide 6 + MoS2
- Taiwan PU Corporation TPUI-G90 High Wear Resistance, Injection Molding Polycaprolactone Base TPU
- Shakespeare Sanstat® CN125 .36mm Nylon 66 Monofilament
- Universal Wire Works 182 Nickel Alloy Welding Wire
- Tisan TISLAMID® 66 25% Glass Fiber Reinforced Flame Retardant (V0). Heat Stabilized Nylon 66
- Zylog Neoplast® 173 C Thermoplastic Vulcanizate
- Borealis Casico™ FR4820 Natural Low Smoke Zero Halogen Flame Retardant Insulation Compound for Building Energy Cables
- Addiplast Addinyl A2 V15 Nylon 66, 15% Glass Filled
Copyright © lookpolymers.com All Rights Reserved