ExxonMobil LL 5100.09 Compounding Resin

Category	Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Compounding Resin
Manufacturer	Exxon Chemical
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LL 5100.09 Compounding Resin.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Product Description: LL 5100.09 is a linear low density polyethylene resin designed to provide good processability and ease of blending. The granular from of LL 5100.09 makes for efficient blending with pigments, slip and antiblock additives.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: NoProcessing Aid: No Thermal Stabilizer: YesApplications: Masterbatch Base Resin Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.925 g/cc	0.0334 lb/in³	ExxonMobil Method
Melt Flow	20 g/10 min @Load 2.16 kg, Temperature 190 °C	20 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	50	50	15s; ASTM D2240
Tensile Strength at Break	7.45 MPa	1080 psi
Tensile Strength, Yield	14.5 MPa	2100 psi	2% Offset; ASTM D638
Elongation at Break	57 %	57 %	ASTM D638
1% Secant Modulus	430 MPa	62400 psi	ASTM D790
Izod Impact, Unnotched	5.34 J/cm	10.0 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	122 °C	252 °F	Peak Melting Temperature; ExxonMobil Method
Brittleness Temperature	-76.1 °C	-105 °F	ASTM D746

Descriptive Properties	Value	Comments
Features	Thermal Stabilizer

Users viewing this material also viewed the following: