ExxonMobil LL 3404.48 Cast Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LL 3404.48 Cast Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LL 3404.48 is a hexene medium density polyethylene cast film grade for applications requiring high strength and high stiffness. It can also be used in blown films. Films produced from this resin exhibit good tensile and puncture resistance properties.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.942 g/cc
0.0340 lb/in³
ExxonMobil Method
Melt Flow 4.3 g/10 min
4.3 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 16.2 MPa
2350 psi
at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD 17.1 MPa
2480 psi
at 2% offset; ASTM D882
Film Elongation at Break, MD 590 %
590 %
ASTM D882
Film Elongation at Break, TD 830 %
830 %
ASTM D882
Puncture Energy 0.791 J
0.583 ft-lb
ExxonMobil
Elmendorf Tear Strength, MD 0.984 g/micron
25.0 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 8.366 g/micron
212.5 g/mil
ASTM D1922
Dart Drop <= 2.46 g/micron
<= 62.5 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 50.5 MPa
7330 psi
ASTM D882
Film Tensile Strength at Break, TD 34.1 MPa
4950 psi
ASTM D882
1% Secant Modulus, MD 381 MPa
55300 psi
ASTM D882
1% Secant Modulus, TD 430 MPa
62300 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 127 °C
261 °F
Peak Melting Temperature; ExxonMobil Method
Crystallization Temperature 114 °C
237 °F
ExxonMobil Method
Optical Properties Metric English Comments
Haze 3.4 %
3.4 %
ASTM D1003
Gloss 82 %
82 %
45°; ASTM D2457
Descriptive Properties Value Comments
Features Thermal Stabilizer
Copyright © lookpolymers.com All Rights Reserved