ExxonMobil LL 1002x79 Blown Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil LL 1002x79 Blown Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LL1002 resins are butene LLDPE designed for blown film process, with good tensile and toughness properties.Information provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ExxonMobil Method |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Antiblock Level | 5000 ppm | 5000 ppm | |
| Slip Level | 1700 ppm | 1700 ppm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 8.48 MPa | 1230 psi | at 2% offset; ASTM D882 |
| Film Tensile Strength at Yield, TD | 8.62 MPa | 1250 psi | at 2% offset; ASTM D882 |
| Film Elongation at Break, MD | 660 % | 660 % | ASTM D882 |
| Film Elongation at Break, TD | 780 % | 780 % | ASTM D882 |
| Puncture Energy | 1.11 J | 0.817 ft-lb | ExxonMobil |
| Elmendorf Tear Strength, MD | 4.72 g/micron | 120 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 13.4 g/micron | 340 g/mil | ASTM D1922 |
| Dart Drop | 2.76 g/micron | 70.0 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 36.5 MPa | 5300 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 26.2 MPa | 3800 psi | ASTM D882 |
| 1% Secant Modulus, MD | 177 MPa | 25700 psi | ASTM D882 |
| 1% Secant Modulus, TD | 196 MPa | 28400 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 123 °C | 253 °F | Peak Melting Temperature; ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 28.7 % | 28.7 % | ASTM D1003 |
| Gloss | 22 % | 22 % | 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Thermal Stabilizer |
Users viewing this material also viewed the following:
- Polykemi AB POLYelast TPE Z805P Thermoplastic Elastomer, SEBS-based
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR N339 Filler
- LyondellBasell Lupolen® 2452 D SW 413 LDPE
- Kazanorgsintez 107-276 Low Density Polyethylene Composition with Improved Processibility
- Karina 829-19/1-IS-RG Cognac PVC Compound
- Tipco Tipcolite® TPF 1612 Phenolic Resin having 320 cps Viscosity containing 64% Solids
- A. Schulman PP 1404-01 Polypropylene High Impact Polypropylene
- DuPont™ Nomex® E56 Paper, 20 mil Nominal Thickness
- ExxonMobil LD 334.57 Clear, High Impact Film Resin
- Fainplast Compounds ARC 10 Rigid PVC, Atoxic for General Purpose
Copyright © lookpolymers.com All Rights Reserved