ExxonMobil LDPE LD 516.LN Low Density Polyethylene Resin

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer	Exxon Chemical
Trade Name	LDPE
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LDPE LD 516.LN Low Density Polyethylene Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: LD 516.LN is a medium MI, low density polyethylene resin designed for use in color concentrates and masterbatches where its flow properties ensure improved processability and uniform dispersion of additives. This resin can also be used in injection molding applications where it offers an outstanding balance of processability and end use performance.Availability: Latin America, North America and South AmericaAdditive: Antiblock: NoSlip: NoThermal Stabilizer: NoApplications: CapsClosuresCompoundingFood Packaging ContainersHouseware ArticlesInjection MoldingMasterbatch Base ResinInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.919 g/cc	0.0332 lb/in³	ExxonMobil method
Melt Flow	9.5 g/10 min @Load 2.16 kg, Temperature 190 °C	9.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	89 @Time 15.0 sec	89 @Time 0.00417 hour	ASTM D2240
Hardness, Shore D	42 @Time 15.0 sec	42 @Time 0.00417 hour	ASTM D2240
Tensile Strength at Break	7.58 MPa	1100 psi	ASTM D638
Tensile Strength, Yield	11.0 MPa	1600 psi	ASTM D638
Elongation at Break	200 %	200 %	ASTM D638
Elongation at Yield	30 %	30 %	ASTM D638
Flexural Modulus, 1% Secant	234 MPa	34000 psi	ASTM D790
Dart Drop, Total Energy	17.6 J @Temperature 22.8 °C	13.0 ft-lb @Temperature 73.0 °F	ASTM D3763
	23.0 J @Temperature -20.0 °C	17.0 ft-lb @Temperature -4.00 °F	ASTM D3763

Thermal Properties	Metric	English	Comments
Melting Point	<= 230 °C	<= 446 °F	Peak Melting Point; ExxonMobil method
Vicat Softening Point	86.1 °C	187 °F	ASTM D1525