- ExxonMobil LD331.08 EVA LD 331.08 Very Clear, High Impact Film Resin
ExxonMobil LD331.08 EVA LD 331.08 Very Clear, High Impact Film Resin
| Category | Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil LD331.08 EVA LD 331.08 Very Clear, High Impact Film Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LD 331 Series films have superior impact strength and heat sealabilityInformation provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | ExxonMobil Method |
| Vinyl Acetate Content | 5.8 % | 5.8 % | ExxonMobil Method |
| Thickness | 38.1 microns | 1.50 mil | |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 7.58 MPa | 1100 psi | at 2% offset; ASTM D882 |
| Film Tensile Strength at Yield, TD | 6.89 MPa | 1000 psi | at 2% offset; ASTM D882 |
| Film Elongation at Break, MD | 240 % | 240 % | ASTM D882 |
| Film Elongation at Break, TD | 670 % | 670 % | ASTM D882 |
| Impact Test | 0.813 J @Temperature -34.0 °C |
0.600 ft-lb @Temperature -29.2 °F |
ASTM D4272 |
| 2.03 J @Temperature 23.0 °C |
1.50 ft-lb @Temperature 73.4 °F |
ASTM D4272 | |
| Elmendorf Tear Strength, MD | 8.27 g/micron | 210 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 2.36 g/micron | 60.0 g/mil | ASTM D1922 |
| Dart Drop | 4.33 g/micron | 110 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 34.5 MPa | 5000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 22.4 MPa | 3250 psi | ASTM D882 |
| 1% Secant Modulus, MD | 138 MPa | 20000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 172 MPa | 25000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 103 °C | 217 °F | Peak Melting Temperature; ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 3.0 % | 3.0 % | ASTM D1003 |
| Gloss | 76 % | 76 % | 45°; ASTM D2457 |
| Transmission, Visible | 90 % | 90 % | clear; thickness not quantified |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Thermal Stabilizer |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8530 (UF) Synthetic Oil
- Pau Tai LB-630, Modifier for PVC
- SABIC Innovative Plastics LNP LUBRICOMP RFL46 PA6.6 (Europe-Africa-Middle East)
- Sharadaa Ceramics REFCAST ULCC90 Low Cement Castables
- Silberline Sparkle Silvex® Premier 950-20-D
- Hexcel® HexForce™ AGP193PBLS Carbon/Wire Fabric
- Loctite® 3035™ Polyolefin Bonder
- Dow DMDB-7950 NT 7 High Density Polyethylene Resin
- EMS-Griltech Grilon® M 369 Black Nylon 6 Fiber (Small Count)
- Arlon 25122R040 0.040" (1.02 mm) Silicone Rubber on Laminated Fluoropolymer Film
Copyright © lookpolymers.com All Rights Reserved